Substituted 5-heteroaryl-2-(2-hydroxyphenyl)-2h-benzotriazole UV absorbers, a process for preparation thereof and compositions stabilized therewith

ABSTRACT

Compounds of formula I or II                    
     where R is a heteroaryl moiety, such as 3-pyridyl, or T is a heteroaryl moiety, such as thien-2,5-diyl, and E 1  and E 2  are independently hydrogen, alkyl, aralkyl and the like, are prepared by reaction of a benzotriazole substituted on the 5-position of the benzo ring by a halogen atom with a heteroarylboronic acid or ester in the presence of a transition-metal catalyst, such as palladium (II) diacetate. The benzotriazole compounds of formula I are particularly efficacious as stabilizers for automotive coatings and candle wax.

The instant invention pertains to novel 5-heteroaryl substituted benzotriazole UV absorbers, to a novel process for their preparation and to compositions stabilized by said benzotriazoles.

BACKGROUND OF THE INVENTION

The benzotriazoles have long been an important class of UV absorbers and have gained wide commercial importance and acceptance for many industrial applications. The prior art is replete with references to their manufacture and utility. However, as requirements become ever more stringent and demanding, the search for still more stable and durable benzotriazoles continues. The gradual phase out of HAPS solvents, such as xylene, because of environmental concerns and their replacement with non-HAPS solvents, such as esters, ethers or ketones, and increased durability requirements for automotive coatings make this search more urgent. Indeed, the automotive industry is most concerned about UVA losses from automotive paints and coatings as seen in the publication by J. L. Gerlock et al., Proc. 36th Annual Tech. Sym. (Cleveland Coating Society), May 18, 1993.

U.S. Pat. Nos. 4,226,763; 4,278,589; 4,315,848; 4,275,004; 4,347,180; 5,554,760; 5,563,242; 5,574,166 and 5,607,987 describe selected benzotriazoles, substituted in the 3-position of the hydroxyphenyl ring by an α-cumyl group, which show very good durability in automotive coatings. These benzotriazoles represent the present state of the art. The instant invention is directed at preparing benzotriazoles which exhibit still better durability and low loss rates from the prior art benzotriazoles.

U.S. Pat. Nos. 5,278,314; 5,280,124; 5,436,349 and 5,516,914 describe red-shifted benzotriazoles. These benzotriazoles are substituted in the 3-position of the phenyl ring with an α-cumyl group and at the 5-position of the benzo ring by thio ethers, alkylsulfonyl or phenylsulfonyl moieties. Red-shifting the benzotriazoles is desirable for spectral reasons. A group at the 5-position which is also electron withdrawing provides additional benefits in low loss rates and durability as found in the instant invention. Missing from these patents are any alkylsulfones with seven or fewer carbon atoms. When such sulfonyl substituents are combined with specifically α-cumyl moieties, extremely durable compounds result which, due to the bulk of the α-cumyl moiety have sufficiently low volatility to be useful in coating and other polymer systems.

The presence of an α-cumyl or phenyl group ortho to the hydroxy group on the phenyl ring exerts a surprisingly large positive effect on benzotriazole photostability in coatings and photographic gel systems. The magnitude of this effect, particularly when compared to a tert-butyl group in that position, is well beyond prediction. The combination of both an electron withdrawing group on the benzo ring and an α-cumyl or phenyl group on the phenyl ring in the same molecule leads to extremely desirable properties in coating systems when high UV absorber permanence is critical.

Novel compounds meeting these parameters as being extremely stable in aggressive use environments constitute a first portion of this invention.

The presence of the electron withdrawing moiety at the 5-position of the benzo ring has a powerful stabilizing effect on benzotriazoles in general and is observed in other polymer systems such as polycarbonate and poly(vinyl chloride) substrates as well. However, the effect of having an α-cumyl or phenyl group ortho to the hydroxy moiety on the phenyl ring is much smaller to non-existent in some polymer systems such as polycarbonate or poly(vinyl chloride) even though critical for coating systems as described above.

In addition to being more photostable, the compounds of this invention are red-shifted, absorbing strongly in the 350-400 nm wavelength range. While such red-shifting is desirable in that a greater portion of the UV spectrum is absorbed, this can also introduce color if the absorption beyond 400 nm is significant. This can limit the use of such compounds, particularly in systems such as polycarbonate glazing applications or present difficulties in various pigmented systems.

It is found that the nature of the substituent ortho to the hydroxyl group on the phenyl ring has an unexpected impact on color imparted to the substrate by the benzotriazole. Thus, relatively subtle differences in substitution on the phenyl ring can have a large impact on the resulting color and the applicability of the benzotriazole in specific color sensitive applications. There are striking differences between having hydrogen, alkyl or α-cumyl at this 3-position.

Furthermore, U.S. Pat. No. 5,977,219 teaches that, when the 5-position of the benzo ring is substituted with a trifluoromethyl group, the resulting benzotriazole not only exhibits the same or greater enhanced stability when incorporated into thermoplastic resins, but also imparts less color than related benzotriazoles substituted at the 5-position with other electron withdrawing moieties such as sulfonyl or carbonyl. These trifluoromethyl compounds also absorb strongly in the 350-400 nm wavelength range despite the low color and are extremely compatible in a wide range of substrates such as acrylic resins, hydrocarbons, polycarbonates and poly(vinyl chloride).

There are a multitude of general references to benzotriazoles having in the 5-position of the benzo ring electron withdrawing groups such as esters, amides, sulfones and the like that are not substituted in the 3-position of the phenyl ring by an α-cumyl or phenyl moiety. In many of these references the broadly described compounds are unexemplified and no teaching or appreciation taught of the positive effect on photostability described in this invention. In any event, the vast majority of these structures fall well outside the scope of instant invention.

Japanese 1996-299547 discloses the use of heterocyclic compounds as non-aqueous electrolytes for lithium batteries. These heterocyclic compounds included benzotriazoles substituted on the benzo ring by hydrogen, methyl, ethyl, amino, hydroxyl, 2-pyridyl or phenyl; and substituted on the hydroxyphenyl ring by at the 5-position by a methyl group and at the 3-position by hydrogen, methyl, ethyl, amino, hydroxyl, 2-pyridyl or phenyl.

A. Suzuki, Pure & Applied Chem., 66, No. 2, 213 (1994) describes a new synthetic method involving the reaction of sterically hindered aryl boronic acids or esters with sterically hindered haloarenes in the presence of palladium (II) catalysts. This reaction has become known as the Suzuki reaction.

B. E. Huff et al., Organic Synthesis, 75, 53 (1998) describe the synthesis of unsymmetrical biaryls using a modified Suzuki cross-coupling to form 4-biphenylcarboxaldehyde.

J. P. Wolfe, et al., J. Am. Chem. Soc., 1999, 121, 9550 describe the use of highly active palladium catalysts for Suzuki coupling reactions.

WO 00/22037 describes the stabilization of solid, shaped and colored wax articles using a malonate UV absorber which may be substituted by a hindered amine group.

Japanese Hei 5-93164 discloses the use of benzotriazole UV absorbers and hindered amines in stabilizing pigmented wax crayons.

Copending U.S. patent applications Ser. Nos. 09/496,084; 09/495,495 and 09/495,496 all describe the stabilization of candle wax using other types of benzotriazole UV absorbers.

DETAILED DESCRIPTION

The instant invention pertains to compounds of formula I or II

wherein

R is 2-pyridyl, 3-pyridyl, 4-pyridyl, 2-thienyl, 3-thienyl, 2-furyl, 3-furyl, 2-pyrrolyl, 3-pyrrolyl, 3-thianaphthenyl, 8-quinolyl, 5-indolyl, 2-selenophenyl, or said pyridyl, thienyl, furyl, pyrrolyl, thianaphthenyl, quinolyl, indolyl or selenophenyl moiety substituted by one to five moieties selected from the group consisting of straight or branched chain alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, R₃S—, R₃SO—, R₃SO₂, aryl of 6 to 10 carbon atoms, perfluoroalkyl of 1 to 12 carbon atoms, halogen, nitro, cyano, carboxyl, triisopropylsilyl, formyl, acetyl, alkoxycarbonyl of 2 to 19 carbon atoms, hydroxyl, alkoxy of 1 to 18 carbon atoms, aryloxy of 6 to 10 carbon atoms, sulfato or phosphato, or where any two substituents from a benzo ring with the heteroaryl moiety to which they are attached,

T is thien-2,5-diyl,

R₃ is alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms or aryl of 6 to 10 carbon atoms,

E₁ is hydrogen, straight or branched chain alkyl of 1 to 24 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 4 alkyl of 1 to 4 carbon atoms,

E₂ is straight or branched chain alkyl of 1 to 24 carbon atoms, straight or branched chain alkenyl of 2 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 3 alkyl of 1 to 4 carbon atoms; or E₂ is alkyl of 1 to 24 carbon atoms or alkenyl of 2 to 18 carbon atoms substituted by one or more —OH, —OCOE₃, —NH₂, —NHCOE₃ or —COOE₃, or mixtures thereof; or said alkyl or said alkenyl interrupted by one or more —O— which can be unsubstituted or substituted by one or more —OH groups; where E₃ is hydrogen or alkyl of 1 to 24 carbon atoms, and where said alkyl is interrupted by one or more —O— and which can be substituted by one or more —OH or —OR₂₁ groups where R₂₁ is alkyl of 1 to 12 carbon atoms; and

with the proviso that, when E₁ is hydrogen, methyl or ethyl and E₂ is methyl or ethyl, R is not 2-pyridyl.

In another embodiment, the compounds of formula I are those where the heterocyclic group R is unsubstituted or is substituted by one moiety selected from the group consisting of methyl, formyl, chloro, acetyl, triisopropylsilyl or tert-butoxycarbonyl; and where E₁ and E₂ are independently straight or branched alkyl of 4 to 24 carbon atoms or phenylalkyl of 7 to 15 carbon atoms.

Still another embodiment are compounds of formula I where R is 3-pyridyl or 3-thienyl; E₁ is α-cumyl; and E₂ is tert-octyl.

The instant invention also pertains to the method of making the instant compounds of formula I or II

where R, T, E₁ and E₂ are as defined above,

by the reaction of an arylboronic acid or ester of formula III or IV

R—B(OR₁)(OR₂)  (III)

(R₂O)(R₁O)B—T—B(OR₁)(OR₂)  (IV)

where R₁ and R₂ are independently hydrogen, alkyl of 1 to 12 carbon atoms, or R₁ and R₂ together are alkylene of 2 to 4 carbon atoms;

with a 5-substituted benzotriazole of formula V

where X is halogen, such as bromo or iodo, or tosylate,

in the presence of an effective amount of a palladium (II) catalyst and optionally in the additional presence of a ligand, such as triphenylphosphine, at between 10 to 100° C., preferably between 50 to 95° C.

When a ligand is used, the ligand is triphenylphosphine, 2-(di-tert-butylphosphino)biphenyl, 1,1′-bis[2,4,8,10-tetrakis(tert-butyl)dibenzo[d,f][1,3,2]dioxaphosphepin-6-yl]ferrocene, tris(2,4-di-tert-butylphenyl)phosphite or 2,2′,2″-nitrilo[triethyl-tris(3,3′,5,5′-tetra-tert-butyl-1,1′biphenyl-2,2′-diyl)phosphite]. In another embodiment, the ligand is triphenylphosphine.

When any of R₁ to R₃ or any of E₁ to E₃ is alkyl, such groups are, straight or branched chain, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, sec-butyl, tert-butyl, tert-amyl, n-hexyl, n-octyl, 2-ethylhexyl, tert-octyl, lauryl, undecyl, tert-dodecyl, tridecyl, n-hexadecyl, n-octadecyl and eicosyl; when any of said radicals is alkenyl, such groups are, for example, allyl, methallyl. 2-n-hexenyl, 4-n-octenyl or oleyl; when any of said radicals is cycloalkyl, such groups are, for example, cyclopentyl,cyclohexyl, cycloheptyl, cyclooctyl or cyclododecyl; when any of said radicals are phenylalkyl, such groups are, for example, benzyl, α-phenethyl, 2-phenethyl, α-methylbenzyl or α,α-dimethylbenzyl; and when any of said radicals is aryl, they are, for example, phenyl, α-naphthyl or β-naphthyl or when substituted by alkyl are, for example, tolyl and xylyl. When alkyl is substituted by one or more —O— groups and/or substituted by one or more —OH, these groups can be hydroxymethyl, 2-hydroxyethyl or 2-hydroxypropyl or can be, for example, —(OCH₂CH₂)_(w)OH or —(OCH₂CH₂)_(w)OR₂₁ where w is 1 to 12 and R₂₁ is alkyl of 1 to 12 carbon atoms; when any of said radicals is halogen, they are, for example, fluoro, chloro, bromo or iodo; when any of said radicals is alkoxycarbonyl, they are, for example, methoxycarbonyl, ethoxycarbonyl, butoxycarbonyl, hexyloxycarbonyl, octyloxycarbonyl, or dodecyloxycarbonyl; when any of said radicals is alkoxy or aryloxy, they are, for example, the same alkyl or same aryl definition as seen above.

The instant invention also pertains to a composition stabilized against thermal, oxidative or light-induced degradation which comprises,

(a) an organic material subject to thermal, oxidative or light-induced degradation, and

(b) an effective stabilizing amount of a compound of formula I or II

wherein

R is 2-pyridyl, 3-pyridyl, 4-pyridyl, 2-thienyl, 3-thienyl, 2-furyl, 3-furyl, 2-pyrrolyl, 3-pyrrolyl, 3-thianaphthenyl, 8-quinolyl, 5-indolyl, 2-selenophenyl, or said pyridyl, thienyl, furyl, pyrrolyl, thianaphthenyl, quinolyl, indolyl or selenophenyl moiety substituted by one to five moieties selected from the group consisting of straight or branched chain alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, R₃S—, R₃SO—, R₃SO₂, aryl of 6 to 10 carbon atoms, trifluoromethyl, halogen, nitro, cyano, carboxyl, triisopropylsilyl, formyl, acetyl, alkoxycarbonyl of 2 to 19 carbon atoms, hydroxyl, alkoxy of 1 to 18 carbon atoms, aryloxy of 6 to 10 carbon atoms, sulfato, phosphato or where any two substituents form a benzoring with the heteroaryl moiety to which they are attached,

T is thien-2,5-diyl,

R₃ is alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms or aryl of 6 to 10 carbon atoms,

E₁ is hydrogen, straight or branched alkyl of 1 to 24 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 4 alkyl of 1 to 4 carbon atoms,

E₂ is straight or branched alkyl chain of 1 to 24 carbon atoms, straight or branched chain alkenyl of 2 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 3 alkyl of 1 to 4 carbon atoms; or E₂ is alkyl of 1 to 24 carbon atoms or alkenyl of 2 to 18 carbon atoms substituted by one or more —OH, —OCOE₃, —NH₂, —NHCOE₃ or —COOE₃, or mixtures thereof; or said alkyl or said alkenyl interrupted by one or more —O— which can be unsubstituted or substituted by one or more —OH groups; where E₃ is hydrogen or alkyl of 1 to 24 carbon atoms, and where said alkyl is interrupted by one or more —O— and which can be substituted by one or more —OH or —OR₂₁ groups where R₂₁ is alkyl of 1 to 12 carbon atoms.

The organic material is a natural, semi-synthetic or synthetic polymer, such as a thermoplastic polymer.

Another embodiment is the polymer which is a polyolefin or polycarbonate, such as polyethylene or polypropylene; still another embodiment is the polymer which is polypropylene; or where the polymer is a styrenic, ABS, a nylon, a polyester such as poly(ethylene terephthalate) or poly(butylene terephthalate), a polyurethane, an acrylate, a rubber modified styrenic, poly(vinyl chloride), poly(vinyl butyral), polyacetal (polyoxymethylene), poly(ethylene naphthalenedicarboxylate), or other blends or copolymers such as poly(ethylene/1,4-cyclohexylenedimethylene terephthalate) PETG or an ionomer.

In another embodiment of the instant invention, the organic material is a resin selected from the group consisting of a thermoset acrylic melamine resin, an acrylic urethane resin, an epoxy carboxy resin, a silane modified acrylic melamine, an acrylic resin with carbamate pendant groups crosslinked with melamine or an acrylic polyol resin crosslinked with melamine containing carbamate groups.

In still another embodiment, the resin is a thermoset acrylic melamine resin or an acrylic urethane resin.

In yet another embodiment of the instant invention, the organic material is a recording material.

The recording materials according to the invention are suitable for pressure-sensitive copying systems, photocopying systems using microcapsules, heat-sensitive copying systems, photographic materials and ink jet printing.

The recording materials according to the invention are distinguished by an unexpected improvement in quality, especially with regard to the fastness to light.

The recording materials according to the invention have the construction known for the particular use. They consist of a customary carrier, for example, paper or plastic film, which has been coated with one or more layers. Depending on the type of material, these layers contain the appropriate necessary components, in the case of photographic materials, for example, silver halide emulsions, dye couplers, dyes and the like. Material particularly suitable for ink jet printing has a layer particularly absorptive for ink on a customary carrier. Uncoated paper can also be employed for ink jet printing. In this case the paper acts at the same time as the carrier material and as the ink-absorbent layer. Suitable material for ink jet printing is, for example, described in U.S. Pat. No. 5,073,448 which is incorporated herein by reference.

The recording material can also be transparent as, for example, in the case of projection films.

The compounds of formula I can be incorporated into the carder material as early as the production of the latter, in the production of paper, for example, being added to the paper pulp. A second method of application is to spray the carder material with an aqueous solution of compounds of formula I or to add the compounds to the coating composition.

Coating compositions intended for transparent recording materials suitable for projection cannot contain any particles which scatter light, such as pigments and fillers.

The dye-binding coating composition can contain a number of other additives, for example, antioxidants, light stabilizers (including also UV absorbers which do not fall under the scope of the UV absorbers of this invention), viscosity improvers, fluorescent brighteners, biocides and/or antistatic agents.

The coating composition is usually prepared as follows: the water-soluble components, for example, the binder, are dissolved in water and stirred together; the solid components, for example, fillers and other additives already described, are dispersed in this aqueous medium; and disperison is advantageously carried out by means of devices, for example, ultrasonic systems, turbine stirrers, homogenizers, colloid mills, bead mills, sand mills, high-speed stirrers and the like. The compounds of formula I can be easily incorporated into the coating composition.

The recording material according to this invention preferably contains 1 to 5000 mg/m², in particular 50-1200 mg/m², of a compound of formula I.

As already mentioned, the recording materials according to the invention embrace a wide field. The compounds of formula I can, for example, be employed in pressure-sensitive copying systems. They can be introduced either into the paper in order to protect the microencapsulated dye precursors there from light, or into the binder of the developer layer in order to protect the dyes formed there.

Photocopying systems using light-sensitive microcapsules which are developed by means of pressure are described in U.S. Pat. Nos. 4,416,966; 4,483,912; 4,352,200; 4,535,050; 4,535,463; 4,551,407; 4,562,137 and 4,608,330; and also in EP-A 139,479; EP-A 162,664; EP-A 164,931; EP-A 237,024; EP-A 237,025 and EP-A 260,129. In all these systems, the compounds can be put into the dye-receiving layer. The compounds can, however, also be put into the donor layer in order to protect the color formers from light.

Photographic materials which can be stabilized are photographic dyes and layers containing such dyes or precursors thereof, for example, photographic paper and films. Suitable materials are, for example, described in U.S. Pat. No. 5,364,749 which is incorporated herein by reference. The compounds of formula I act here as a UV filter against electrostatic flashes. In color photographic materials, couplers and dyes are also protected against photochemical decomposition.

The instant compounds can be used for all types of color photographic materials. For example, they can be employed for color paper, color reversal paper, direct-positive color material, color negative film, color positive film, color reversal film and the like. They are preferably used inter alia for photographic color material which contains a reversal substrate or form positives.

Color-photographic recording materials usually contain, on a support, a blue-sensitive and/or a green-sensitive and/or a red-sensitive silver halide emulsion layer and, if desired, a protection layer, with the instant compounds being, preferably, either in the green-sensitive or the red-sensitive layer or in a layer between the green-sensitive and the red-sensitive layer or in a layer on top of the silver halide emulsion layers.

The compounds of formula I can also be employed in recording materials based on the principles of photopolymerization, photoplasticization or the rupture of microcapsules, or in cases where heat-sensitive and light-sensitive diazonium salts, leuko dyes having an oxidizing agent or dye lactones: having Lewis acids are used.

Furthermore, the instant compounds can be employed in recording materials for dye diffusion transfer printing, thermal wax transfer printing and non-matrix printing and for use with electrostatic, electrographic, electrophoretic, magnetographic and laser-electrophotographic printers and pen-plotters. Of the above, recording materials for dye diffusion transfer printing are preferred, for example, as described in EP-A 507,734.

The instant compounds can also be employed in inks, such as for ink jet printing, for example, as described in U.S. Pat. No. 5,098,477 which is incorporated herein by reference.

The instant compounds also are effective in the protection of dyes present in candle wax from premature degradation and fading.

The instant compounds of formula I are also useful in adhesives used in solar films, optical films and other laminated structures against the adverse effects of ultraviolet light and actinic radiation.

The compounds of this invention exhibit superior hydrolytic stability, handling and storage stability as well as good resistance to extractability when present in a stabilized composition.

The methodology to make the instant compounds is described in the prior art. The intermediates needed to make the instant compounds are largely items of commerce.

Compounds in which one of X and Y is —O—; and those in which both X and Y are —O— represent other embodiments of the instant invention.

In general polymers which can be stabilized include

1. Polymers of monoolefins and diolefins, for example polypropylene, polyisobutylene, polybut-1-ene, poly-4-methylpent-1-ene, polyisoprene or polybutadiene, as well as polymers of cycloolefins, for instance of cyclopentene or norbornene, polyethylene (which optionally can be crosslinked), for example high density polyethylene (HDPE), low density polyethylene (LDPE), linear low density polyethylene (LLDPE), branched low density polyethylene (BLDPE).

Polyolefins, i.e. the polymers of monoolefins exemplified in the preceding paragraph, preferably polyethylene and polypropylene, can be prepared by different, and especially by the following, methods:

a) radical polymerisation (normally under high pressure and at elevated temperature).

b) catalytic polymerisation using a catalyst that normally contains one or more than one metal of groups IVb, Vb, VIb or VIII of the Periodic Table. These metals usually have one or more than one ligand, typically oxides, halides, alcoholates, esters, ethers, amines, alkyls, alkenyls and/or aryls that may be either π- or σ-coordinated. These metal complexes may be in the free form or fixed on substrates, typically on activated magnesium chloride, titanium(III) chloride, alumina or silicon oxide. These catalysts may be soluble or insoluble in the polymerisation medium. The catalysts can be used by themselves in the polymerisation or further activators may be used, typically metal alkyls, metal hydrides, metal alkyl halides, metal alkyl oxides or metal alkyloxanes, said metals being elements of groups Ia, IIa and/or IIIa of the Periodic Table. The activators may be modified conveniently with further ester, ether, amine or silyl ether groups. These catalyst systems are usually termed Phillips, Standard Oil Indiana, Ziegler (-Natta), TNZ (DuPont), metallocene or single site catalysts (SSC).

2. Mixtures of the polymers mentioned under 1), for example mixtures of polypropylene with polyisobutylene, polypropylene with polyethylene (for example PP/HDPE, PP/LDPE) and mixtures of different types of polyethylene (for example LDPE/HDPE).

3. Copolymers of monoolefins and diolefins with each other or with other vinyl monomers, for example ethylene/propylene copolymers, linear low density polyethylene (LLDPE) and mixtures thereof with low density polyethylene (LDPE), propylene/but-1-ene copolymers, propylene/isobutylene copolymers, ethylene/but-1-ene copolymers, ethylene/hexene copolymers, ethylene/methylpentene copolymers, ethylene/heptene copolymers, ethylene/octene copolymers, propylene/butadiene copolymers, isobutylene/isoprene copolymers, ethylene/alkyl acrylate copolymers, ethylene/alkyl methacrylate copolymers, ethylene/vinyl acetate copolymers and their copolymers with carbon monoxide or ethylene/acrylic acid copolymers and their salts (ionomers) as well as terpolymers of ethylene with propylene and a diene such as hexadiene, dicyclopentadiene or ethylidene-norbornene; and mixtures of such copolymers with one another and with polymers mentioned in 1) above, for example polypropylene/ethylene-propylene copolymers, LDPE/ethylene-vinyl acetate copolymers (EVA), LDPE/ethylene-acrylic acid copolymers (EAA), LLDPE/EVA, LLDPE/EAA and alternating or random polyalkylene/carbon monoxide copolymers and mixtures thereof with other polymers, for example polyamides.

4. Hydrocarbon resins (for example C₅-C₉) including hydrogenated modifications thereof (e.g. tackifiers) and mixtures of polyalkylenes and starch.

5. Polystyrene, poly(p-methylstyrene), poly(α-methylstyrene).

6. Copolymers of styrene or α-methylstyrene with dienes or acrylic derivatives, for example styrene/butadiene, styrene/acrylonitrile, styrene/alkyl methacrylate, styrene/butadiene/alkyl acrylate, styrene/butadiene/alkyl methacrylate, styrene/maleic anhydride, styrene/acrylonitrile/methyl acrylate; mixtures of high impact strength of styrene copolymers and another polymer, for example a polyacrylate, a diene polymer or an ethylene/propylene/diene terpolymer, and block copolymers of styrene such as styrene/butadiene/styrene, styrene/isoprene/styrene, styrene/ethylene/butylene/styrene or styrene/ethylene/propylene/styrene.

7. Graft copolymers of styrene or α-methylstyrene, for example styrene on polybutadiene, styrene on polybutadiene-styrene or polybutadiene-acrylonitrile copolymers; styrene and acrylonitrile (or methacrylonitrile) on polybutadiene; styrene, acrylonitrile and methyl methacrylate on polybutadiene; styrene and maleic anhydride on polybutadiene; styrene, acrylonitrile and maleic anhydride or maleimide on polybutadiene; styrene and maleimide on polybutadiene; styrene and alkyl acrylates or methacrylates on polybutadiene; styrene and acrylonitrile on ethylene/propylene/diene terpolymers; styrene and acrylonitrile on polyalkyl acrylates or polyalkyl methacrylates, styrene and acrylonitrile on acrylate/butadiene copolymers, as well as mixtures thereof with the copolymers listed under 6), for example the copolymer mixtures known as ABS, MBS, ASA or AES polymers.

8. Halogen-containing polymers such as polychloroprene, chlorinated rubbers, chlorinated or sulfochlorinated polyethylene, copolymers of ethylene and chlorinated ethylene, epichlorohydrin homo- and copolymers, especially polymers of halogen-containing vinyl compounds, for example polyvinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polyvinylidene fluoride, as well as copolymers thereof such as vinyl chloride/vinylidene chloride, vinyl chloride/vinyl acetate or vinylidene chloride/vinyl acetate copolymers.

9. Polymers derived from α,β-unsaturated acids and derivatives thereof such as polyacrylates and polymethacrylates; polymethyl methacrylates, polyacrylamides and polyacrylonitriles, impact-modified with butyl acrylate.

10. Copolymers of the monomers mentioned under 9) with each other or with other unsaturated monomers, for example acrylonitrile/butadiene copolymers, acrylonitrile/alkyl acrylate copolymers, acrylonitrile/alkoxyalkyl acrylate or acrylonitrile/vinyl halide copolymers or acrylonitrile/alkyl methacrylate/butadiene terpolymers.

11. Polymers derived from unsaturated alcohols and amines or the acyl derivatives or acetals thereof, for example polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate or polyallyl melamine; as well as their copolymers with olefins mentioned in 1) above.

12. Homopolymers and copolymers of cyclic ethers such as polyalkylene glycols, polyethylene oxide, polypropylene oxide or copolymers thereof with bisglycidyl ethers.

13. Polyacetals such as polyoxymethylene and those polyoxymethylenes which contain ethylene oxide as a comonomer, polyacetals modified with thermoplastic polyurethanes, acrylates or MBS.

14. Polyphenylene oxides and sulfides, and mixtures of polyphenylene oxides with styrene polymers or polyamides.

15. Polyurethanes derived from hydroxyl-terminated polyethers, polyesters or polybutadienes on the one hand and aliphatic or aromatic polyisocyanates on the other, as well as precursors thereof.

16. Polyamides and copolyamides derived from diamines and dicarboxylic acids and/or from aminocarboxylic acids or the corresponding lactams, for example polyamide 4, polyamide 6, polyamide 6/6, 6/10, 6/9, 6/12, 4/6, 12/12, polyamide 11, polyamide 12, aromatic polyamides starting from m-xylene diamine and adipic acid; polyamides prepared from hexamethylenediamine and isophthalic or/and terephthalic acid and with or without an elastomer as modifier, for example poly-2,4,4,-trimethylhexamethylene terephthalamide or poly-m-phenylene isophthalamide; and also block copolymers of the aforementioned polyamides with polyolefins, olefin copolymers, ionomers or chemically bonded or grafted elastomers; or with polyethers, e.g. with polyethylene glycol, polypropylene glycol or polytetramethylene glycol; as well as polyamides or copolyamides modified with EPDM or ABS; and polyamides condensed during processing (RIM polyamide systems).

17. Polyureas, polyimides, polyamide-imides and polybenzimidazoles.

18. Polyesters derived from dicarboxylic acids and diols and/or from hydroxycarboxylic acids or the corresponding lactones, for example polyethylene terephthalate, polybutylene terephthalate, poly-1,4-dimethylolcyclohexane terephthalate and polyhydroxybenzoates, as well as block copolyether esters derived from hydroxyl-terminated polyethers; and also polyesters modified with polycarbonates or MBS.

19. Polycarbonates and polyester carbonates.

20. Polysulfones, polyether sulfones and polyether ketones.

21. Crosslinked polymers derived from aldehydes on the one hand and phenols, ureas and melamines on the other hand, such as phenol/formaldehyde resins, urea/formaldehyde resins and melamine/formaldehyde resins.

22. Drying and non-drying alkyd resins.

23. Unsaturated polyester resins derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols and vinyl compounds as crosslinking agents, and also halogen-containing modifications thereof of low flammability.

24. Crosslinkable acrylic resins derived from substituted acrylates, for example epoxy acrylates, urethane acrylates or polyester acrylates.

25. Alkyd resins, polyester resins and acrylate resins crosslinked with melamine resins, urea resins, polyisocyanates or epoxy resins.

26. Crosslinked epoxy resins derived from polyepoxides, for example from bisglycidyl ethers or from cycloaliphatic diepoxides.

27. Natural polymers such as cellulose, rubber, gelatin and chemically modified homologous derivatives thereof, for example cellulose acetates, cellulose propionates and cellulose butyrates, or the cellulose ethers such as methyl cellulose; as well as rosins and their derivatives.

28. Blends of the aforementioned polymers (polyblends), for example PP/EPDM, Polyamide/EPDM or ABS, PVC/EVA, PVC/ABS, PVC/MBS, PC/ABS, PBTP/ABS, PC/ASA, PC/PBT, PVC/CPE, PVC/acrylates, POM/thermoplastic PUR, PC/thermoplastic PUR, POM/acrylate, POM/MBS, PPO/HIPS, PPO/PA 6.6 and copolymers, PA/HDPE, PA/PP, PA/PPO.

29. Naturally occurring and synthetic organic materials which are pure monomeric compounds or mixtures of such compounds, for example mineral oils, animal and vegetable fats, oil and waxes, or oils, fats and waxes based on synthetic esters (e.g. phthalates, adipates, phosphates or trimellitates) and also mixtures of synthetic esters with mineral oils in any weight ratios, typically those used as spinning compositions, as well as aqueous emulsions of such materials.

30. Aqueous emulsions of natural or synthetic rubber, e.g. natural latex or latices of carboxylated styrene/butadiene copolymers.

31. Polysiloxanes such as the soft, hydrophilic polysiloxanes described, for example, in U.S. Pat. No. 4,259,467; and the hard polyorganosiloxanes described, for example, in U.S. Pat. No. 4,355,147.

32. Polyketimines in combination with unsaturated acrylic polyacetoacetate resins or with unsaturated acrylic resins. The unsaturated acrylic resins include the urethane acrylates, polyether acrylates, vinyl or acryl copolymers with pendant unsaturated groups and the acrylated melamines. The polyketimines are prepared from polyamines and ketones in the presence of an acid catalyst.

33. Radiation curable compositions containing ethylenically unsaturated monomers or oligomers and a polyunsaturated aliphatic oligomer.

34. Epoxymelamine resins such as light-stable epoxy resins crosslinked by an epoxy functional coetherified high solids melamine resin such as LSE-4103 (Monsanto).

In general, the compounds of the present invention are employed in from about 0.01 to about 5% by weight of the stabilized composition, although this will vary with the particular substrate and application. An advantageous range is from about 0.05 to about 3%, and especially 0.05 to about 1%. However, some high performance films or in UV absorbing layers of laminates such as those produced by coextrusion may contain from 5-15% by weight of the instant compounds. Concentrations of 5-10% by weight are typical in certain coextrusion applications.

The stabilizers of the instant invention may readily be incorporated into the organic polymers by conventional techniques, at any convenient stage prior to the manufacture of shaped articles therefrom. For example, the stabilizer may be mixed with the polymer in dry powder form, or a suspension or emulsion of the stabilizer may be mixed with a solution, suspension, or emulsion of the polymer. The resulting stabilized polymer compositions of the invention may optionally also contain from about 0.01 to about 5%, preferably from about 0.025 to about 2%, and especially from about 0.1 to about 1% by weight of various conventional additives, such as the materials listed below, or mixtures thereof.

1. Antioxidants

1.1. Alkylated Monophenols, for Example,

2,6-di-tert-butyl-4-methylphenol

2-tert-butyl-4,6-dimethylphenol

2,6-di-tert-butyl-4-ethylphenol

2,6-tert-butyl-4-n-butylphenol

2,6-di-tert-butyl-4-i-butylphenol

2,6-di-cyclopentyl-4-methylphenol

2-(α-methylcyclohexyl)-4,6-dimethylphenol

2,6-di-octadecyl-4-methylphenol

2,4,6-tri-cyclohexylphenol

2,6-di-tert-butyl-4-methoxymethylphenol

1.2. Alkylated Hydroquinones, for Example,

2,6-di-tert-butyl-4-methoxyphenol

2,5-di-tert-butyl-hydroquinone

2,5-di-tert-amyl-hydroquinone

2,6-diphenyl-4-octadecyloxyphenol

1.3. Hydroxylated Thiodiphenyl Ethers, for Example,

2,2′-thio-bis-(6-tert-butyl-4-methylphenol)

2,2′-thio-bis-(4-octylphenol)

4,4′-thio-bis-(6-tert-butyl-3-methylphenol)

4,4′-thio-bis-(6-tert-butyl-2-methylphenol)

1.4. Alkylidene-bisphenols, for Example,

2,2′-methylene-bis-(6-tert-butyl-4-methylphenol)

2,2′-methylene-bis-(6-tert-butyl-4-ethylphenol)

2,2′-methylene-bis-[4-methyl-6-(α-methylcyclohexyl)-phenol]

2,2′-methylene-bis-(4-methyl-6-cyclohexylphenol)

2,2′-methylene-bis-(6-nonyl-4-methylphenol)

2,2′-methylene-bis-[6-(α-methylbenzyl)-4-nonylphenol]

2,2′-methylene-bis-[6-(α,α-dimethylbenzyl)-4-nonylphenol]

2,2′-methylene-bis-(4,6-di-tert-butylphenol)

2,2′-ethylidene-bis-(4,6-di-tert-butylphenol)

2,2′-ethylidene-bis-(6-tert-butyl-4-isobutylphenol)

4,4′-methylene-bis-(2,6-di-tert-butylphenol)

4,4′-methylene-bis-(6-tert-butyl-2-methylphenol)

1,1-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-butane

2,6-di-(3-tert-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol

1,1,3-tris-(5-tert-butyl-4-hydroxy-2-methylphenyl)-butane

1,1-bis-(5-tert-butyl-4-hydroxy-2-methylphenyl)-3-n-dodecylmercaptobutane

ethyleneglycol bis-[3,3-bis-(3′-tert-butyl-4′-hydroxyphenyl)-butyrate]

di-(3-tert-butyl-4-hydroxy-5-methylphenyl)-dicyclopentadiene

di-[2-(3′-tert-butyl-2′-hydroxy-5′-methyl-benzyl)-6-tert-butyl-4-methylphenyl]terephthalate.

1.5. Benzyl Compounds, for Example,

1,3,5-tri-(3,5-di-tert-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene

di-(3,5-di-tert-butyl-4-hydroxybenzyl)sulfide

3,5-di-tert-butyl-4-hydroxybenzyl-mercapto-acetic acid isooctyl ester

bis-(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)dithiol terephthalate

1,3,5-tris-(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate

1,3,5-tris-(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)isocyanurate

3,5di-tert-butyl-4-hydroxybenzyl-phosphoric acid dioctadecyl ester

3,5di-tert-butyl-4-hydroxybenzyl-phosphoric acid monoethyl ester, calcium-salt

1.6. Acylaminophenols, for Example,

4-hydroxy-lauric acid anilide

4-hydroxy-stearic acid anilide

2,4-bis-octylmercapto-6-(3,5-tert-butyl-4-hydroxyanilino)-s-triazine

octyl-N-(3,5-i-tert-butyl-4-hydroxyphenyl)-carbamate

1.7. Esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic Acid with Monohydric or Polyhydric Alcohols, for Example,

methanol

octadecanol

1,6-hexanediol

neopentyl glycol

thiodiethylene glycol

triethanolamine

diethylene glycol

triethylene glycol

pentaerythritol

tris-hydroxyethyl isocyanurate

di-hydroxyethyl oxalic acid diamide

triisopropanolamine

1.8. Esters of β-(5-tert-butyl-4-hydroxy-3-methylphenyl)-propionic Acid with Monohydric or Polyhydric Alcohols, for Example,

methanol

octadecanol

1,6hexanediol

neopentyl glycol

thiodiethylene glycol

triethanolamine

diethylene glycol

triethylene glycol

pentaerythritol

tris-hydroxyethyl isocyanurate

di-hydroxyethyl oxalic acid diamide

triisopropanolamine

1.9. Amides of β-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic Acid for Example,

N,N′di-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hexamethylenediamine

N,N′di-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-trimethylenediamine

N,N′-i-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hydrazine

1.10 Diarylamines, for Example,

diphenylamine, N-phenyl-1-naphthylamine, N-(4-tert-octylphenyl)-1-naphthylamine, 4,4′-di-tert-octyl-diphenylamine, reaction product of N-phenylbenzylamine and 2,4,4-trimethylpentene, reaction product of diphenylamine and 2,4,4-trimethylpentene, reaction product of N-phenyl-1-naphthylamine and 2,4,4-trimethylpentene.

2. UV Absorbers and Light Stabilizers

2.1. 2-(2′-Hydroxyphenyl)-benzotriazoles, for Example,

the 5′-methyl-, 3′,5′-di-tert-butyl-, 5′-tert-butyl-, 5′-(1,1,3,3-tetramethylbutyl)-, 5-chloro-3′,5′-di-tert-butyl-, 5-chloro-3′-tert-butyl-5′-methyl-, 3′-sec-butyl-5′-tert-butyl-, 4′-octoxy, 3′,5′-di-tert-amyl-, 3′,5′-bis-(α,α-dimethylbenzyl), 3′-tert-butyl-5′-(2-(omega-hydroxy-octa-(ethyleneoxy)carbonyl-ethyl)-, 3′-dodecyl-5′-methyl-, and 3′-tert-butyl-5′-(2-octyloxycarbonyl)ethyl-, and dodecylated-5′-methyl derivatives.

2.2.2-Hydroxy-benzophenones, for Example,

the 4-hydroxy-, 4-methoxy-, 4-octoxy, 4-decyloxy-, 4-dodecyloxy-, 4-benzyloxy, 4,2′,4′-trihydroxy- and 2′-hydroxy-4,4′-dimethoxy derivatives.

2.3. Esters of Optionally Substituted Benzoic Acids for Example,

phenyl salicylate, 4-tert-butylphenyl salicylate, octylphenyl salicylate, dibenzoylresorcinol, bis-(4-tert-butylbenzoyl)-resorcinol, benzoylresorcinol, 3,5-di-tert-butyl-4-hydroxybenzoic acid 2,4-di-tert-butylphenyl ester and 3,5di-tert-butyl-4-hydroxybenzoic acid hexadecyl ester.

2.4. Acrylates, for Example,

α-cyano-β,β-diphenylacrylic acid ethyl ester or isooctyl ester, α-carbomethoxy-cinnamic acid methyl ester, α-cyano-β-methyl-p-methoxy-cinnamic acid methyl ester or butyl ester, α-carbomethoxy-p-methoxy-cinnamic acid methyl ester, N-(β-carbomethoxy-β-cyanovinyl)-2-methyl-indoline.

2.5. Nickel Compounds, for Example,

nickel complexes of 2,2′-thio-bis-[4-(1,1,3,3-tetramethylbutyl)-phenol], such as the 1:1 or 1:2 complex, optionally with additional ligands such as n-butylamine, triethanolamine or N-cyclohexyl-diethanolamine, nickel dibutyldithiocarbamate, nickel salts of 4-hydroxy-3,5-di-tert-butylbenzylphosphonic acid monoalkyl esters, such as of the methyl, ethyl or butyl ester, nickel complexes of ketoximes such as of 2-hydroxy-4-methyl-phenyl undecyl ketoxime, nickel complexes of 1-phenyl-4-lauroyl-5-hydroxy-pyrazole, optionally with additional ligands.

2.6. Sterically Hindered Amines, for Example

bis-(2,2,6,6-tetramethylpiperidyl)sebacate, bis-(1,2,2,6,6-pentamethylpiperidyl)sebacate, n-butyl-3,5-di-tert.butyl-4-hydroxybenzyl malonic acid bis-(1,2,2,6,6-pentanemethylpiperidyl)ester, condensation product of 1-hydroxyethyl-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, condensation product of N,N′-(2,2,6,6-tetra-methylpiperidyl)-hexamethylenediamine and 4-tert-octylamino-2,6-dichloro-s-triazine, tris-(2,2,6,6-tetramethylpiperidyl)-nitrilotriacetate, tetrakis-(2,2,6,6-tetramethyl-4-piperidyl) 1,2,3,4-butanetetracarboxylate, 1,1′(1,2-ethanediyl)-bis-(3,3,5,5-tetramethylpiperazinone), bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, 1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine.

2.7. Oxalic Acid Diamides, for Example,

4,4′-di-octyloxy-oxanilide, 2,2′-di-octyloxy-5,5′-di-tert-butyl-oxanilide, 2,2′-di-dodecyloxy-5,5′-di-tert-butyl-oxanilide, 2-ethoxy-2′-ethyl-oxanilide, N,N′-bis (3-dimethylaminopropyl)-oxalamide, 2-ethoxy-5-tert-butyl-2′-ethyloxanilide and its mixture with 2-ethoxy-2′-ethyl-5,4′-di-tert-butyloxanilide and mixtures of ortho- and para-methoxy- as well as of o- and p-ethoxy-substituted oxanilides.

2.8. Hydroxyphenyl-s-triazines, for Example

2,6bis-(2,4-dimethylphenyl)-4-(2-hydroxy-4-octyloxyphenyl)-s-triazine; 2,6-bis-(2,4-dimethylphenyl)-4-(2,4-dihydroxyphenyl)-s-triazine; 2,4-bis(2,4-dihydroxyphenyl)-6-(4-chlorophenyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-hydroxyethoxy)phenyl]-6-(4-chlorophenyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-hydroxy-4-(2-hydroxyethoxy)phenyl]-6-(2,4-dimethylphenyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-hydroxyethoxy)-phenyl]-6(4-bromophenyl)-s-triazine; 2,4-bis[2-hydroxy-4-(2-acetoxyethoxy)phenyl]-6-(4-chlorophenyl)-s-triazine, 2,4-bis(2,4-dihydroxyphenyl)-6-(2,4-dimethylphenyl)-s-triazine.

3. Metal Deactivators, for Example,

N,N′-diphenyloxalic acid diamide, N-salicylal-N′-salicyloylhydrazine, N,N′-bis-salicyloylhydrazine, N,N′-bis-(3,5-di-tert-butyl-4-hydroxyphenylpropionyl)-hydrazine, 3-salicyloylamino-1,2,4-triazole, bis-benzylidene-oxalic acid dihydrazide.

4. Phosphites and Phosphonites, for Example,

triphenyl phosphite, diphenylalkyl phosphites, phenyldialkyl phosphites, tri-(nonylphenyl)phosphite, trilauryl phosphite, trioctadecyl phosphite, di-stearyl-pentaerythritol diphosphite, tris-(2,4-di-tert-butylphenyl)phosphite, di-isodecylpentaerythritol diphosphite, di-(2,4,6-tri-tert-butylphenyl)-pentaerythritol diphosphite, di-(2,4-di-tert-butyl-6-methylphenyl)-pentaerythritol diphosphite, di-(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, tristearyl-sorbitol triphosphite, tetrakis-(2,4-di-tert-butylphenyl) 4,4′-diphenylylenediphosphonite.

5. Compounds which Destroy Peroxide, for Example,

esters of β-thiodipropionic acid, for example the lauryl, stearyl, myristyl or tridecyl esters, mercapto-benzimidazole or the zinc salt of 2-mercaptobenzimidazole, zinc dibutyl-dithiocarbamate, dioctadecyl disulfide, pentaerythritol tetrakis-(β-dodecylmercapto)-propionate.

6. Hydroxylamines, for Example,

N,N-dibenzylhydroxylamine, N,N-diethylhydroxylamine, N,N-dioctylhydroxylamine, N,N-dilaurylhydroxylamine, N,N-ditetradecylhydroxylamine, N,N-dihexadecylhydroxylamine, N,N-dioctadecylhydroxylamine, N-hexadecyl-N-octadecylhydroxylamine, N-heptadecyl-N-octadecylhydroxylamine, N,N-dialkylhydroxylamine derived from hydrogenated tallow amine.

7. Nitrones, for Example,

N-benzyl-alpha-phenyl nitrone, N-ethyl-alpha-methyl nitrone, N-octyl-alpha-heptyl nitrone, N-lauryl-alpha-undecyl nitrone, N-tetradecyl-alpha-tridecyl nitrone, N-hexadecyl-alpha-pentadecyl nitrone, N-octadecyl-alpha-heptadecylnitrone, N-hexadecyl-alpha-heptadecyl nitrone, N-octadecyl-alpha-pentadecyl nitrone, N-heptadecyl-alpha-heptadecyl nitrone, N-octadecyl-alpha-hexadecyl nitrone, nitrone derived from N,N-dialkylhydroxylamine derived from hydrogenated tallow amine.

8. Amine Oxides, for Example,

tridecyl amine oxide, tridodecyl amine oxide, trihexadecyl amine oxide, tri(C₁₂-C₁₄ alkyl)amine oxide, tri(C₁₆-C₁₈ alkyl)amine oxide, tri(C₂₀-C₂₂ alkyl)amine oxide, di(C₁₂-C₁₄ alkyl)methyl amine oxide, di(C₁₆-C₁₈ alkyl)methyl amine oxide, di(C₂₀-C₂₂ alkyl)methyl amine oxide, di(tallow alkyl)methyl amine oxide, di(coco alkyl)methyl amine oxide.

9. Polyamide Stabilizers, for Example

copper salts in combination with iodides and/or phosphorus compounds and salts of divalent manganese.

10. Basic Co-stabilizers, for Example,

melamine, polyvinylpyrrolidone, dicyandiamide, triallyl cyanurate, urea derivatives, hydrazine derivatives, amines, polyamides, polyurethanes, alkali metal salts and alkaline earth metal salts of higher fatty acids for example Ca stearate, Zn stearate, Mg stearate, Na ricinoleate and K palmitate, antimony pyrocatecholate or zinc pyrocatecholate.

11. Nucleating Agents, for Example,

4-tert-butyl-benzoic acid, adipic acid, diphenylacetic acid.

12. Fillers and Reinforcing Agents, for Example,

calcium carbonate, silicates, glass fibers, asbestos, talc, kaolin, mica, barium sulfate, metal oxides and hydroxides, carbon black, graphite.

13. Other Additives, for Example,

plasticizers, lubricants, emulsifiers, pigments, optical brighteners, flameproofing agents, anti-static agents, blowing agents and thiosynergists such as dilauryl thiodipropionate or distearyl thiodipropionate.

14. Benzofuranones and Indolinones, for Example

those disclosed in U.S. Pat. Nos. 4,325,863, 4,338,244 or 5,175,312, or 3-[4-(2-acetoxyethoxy)phenyl]-5,7-di-tert-butyl-benzofuran-2-one, 5,7-di-tert-butyl-3-[4-(2-stearoyloxyethoxy)phenyl]benzofuran-2-one, 3,3′-bis[5,7-di-tert-butyl-3-(4-[2-hydroxyethoxy]phenyl)benzofuran-2-one], 5,7-di-tert-butyl-3-(4-ethoxyphenyl)-benzofuran-2-one, 3-(4-acetoxy-3,5-dimethylphenyl)-5,7-di-tert-butyl-benzofuran-2-one, 3-(3,5dimethyl-4-pivaloyloxyphenyl)-5,7-di-tert-butyl-benzofuran-2-one.

The co-stabilizers, with the exception of the benzofuranones listed under 13, are added for example in concentrations of 0.01 to 10%, relative to the total weight of the material to be stabilized.

Further preferred compositions comprise, in addition to components (a) and (b) further additives, in particular phenolic antioxidants, light stabilizers or processing stabilizers.

Particularly preferred additives are phenolic antioxidants (item 1 of the list), sterically hindered amines (item 2.6 of the list), phosphites and phosphonites (item 4 of the list), UV absorbers (item 2 of the list) and peroxide-destroying compounds (item 5 of the list).

Additional additives (stabilizers) which are also particularly preferred are benzofuran-2-ones, such as described, for example, in U.S. Pat. Nos. 4,325,863, 4,338,244 or 5,175,312.

The phenolic antioxidant of particular interest is selected from the group consisting of n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, neopentanetetrayl tetrakis(3,5-di-tert-butyl-4-hydroxyhydrocinammate), di-n-octadecyl 3,5di-tert-butyl-4-hydroxybenzylphosphonate, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, thiodiethylene bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), 1,3,5-trimethyl-2,4,6tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 3,6-dioxaoctamethylene bis(3-methyl-5-tert-butyl-4-hydroxyhydrocinnamate), 2,6-di-tert-butyl-p-cresol, 2,2′-ethylidene-bis(4,6-di-tert-butylphenol), 1,3,5-tris(2,6-dimethyl4-tert-butyl-3-hydroxybenzyl)isocynurate, 1,1,3,-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane, 1,3,5-tris[2-(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyloxy)ethyl]isocyanurate, 3,5-di-(3,5-di-tert-butyl-4-hydroxybenzyl)mesitol, hexamethylene bis(3,5di-tert-butyl-4-hydroxyhydrocinnamate), 1-(3,5-di-tert-butyl-4-hydroxyanilino)-3,5-di(octylthio)-s-triazine, N,N′-hexamethylene-bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamamide), calcium bis(ethyl 3,5-tert-butyl-4-hydroxybenzylphosphonate), ethylene bis[3,3-di(3-tert-butyl-4-hydroxyphenyl)butyrate], octyl 3,5-di-tert-butyl-4-hydroxybenzylmercaptoacetate, bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hydrazide, and N,N′-bis[2-(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyloxy)-ethyl]-oxamide.

A most preferred phenolic antioxidant is neopentanetetrayl tetrakis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate), n-octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate, 2,6-di-tert-butyl-p-cresol or 2,2′-ethylidene-bis(4,6-di-tert-butylphenol).

The hindered amine compound of particular interest is selected from the group consisting of bis(2,2,6,6-tetramethylpiperidin-4-yl)sebacate, bis(1,2,2,6,6-pentamethylpiperidin-4-yl)sebacate, di(1,2,2,6,6-pentamethylpiperidin-4-yl)(3,5-di-tert-butyl-4-hydroxybenzyl)butylmalonate, 4-benzoyl-2,2,6,6-tetramethylpiperidine, 4-stearyloxy-2,2,6,6-tetramethylpiperidine, 3-n-octyl-7,7,9,9-tetramethyl-1,3,8-triaza-spiro[4.5]decane-2,4-dione, tris(2,2,6,6-tetramethylpiperidin-4-yl)nitrilotriacetate, 1,2-bis(2,2,6,6-tetramethyl-3-oxopiperazin-4-yl)ethane, 2,2,4,4-tetramethyl-7-oxa-3,20-diaza-21-oxodispiro[5.1.11.2]heneicosane, polycondensation product of 2,4-dichloro-6-tert-octylamino-s-triazine and 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine), polycondensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, polycondensation product of 4,4′-hexamethylenebis-(amino-2,2,6,6-tetramethylpiperidine) and 1,2-dibromoethane, tetrakis(2,2,6,6-tetramethylpiperidin-4-yl) 1,2,3,4-butanetetracarboxylate, tetrakis(1,2,2,6,6-pentamethylpiperidin-4-yl) 1,2,3,4-butanetetracarboxylate, polycondensation product of 2,4-dichloro-6-morpholino-s-triazine and 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine), N,N′,N″,N′″-tetrakis[(4,6-bis(butyl-1,2,2,6,6-pentamethylpiperidin-4-yl)-amino-s-triazin-2-yl]-1,10-diamino-4,7-diazadecane, mixed [2,2,6,-tetramethylpiperidin-4-yl/β,β,β′β′, -tetramethyl-3,9-(2,4,8,10-tetraoxaspiro[5.5]-undecane)diethyl]1,2,3,4-butanetetracarboxylate, mixed [1,2,2,6,6-pentamethylpiperidin-4-yl/β,β,β′,β′-tetramethyl-3,9-(2,4,8,10-tetraoxaspiro[5.5]-undecane)diethyl]1,2,3,4-butanetetracarboxylate, octamethylene bis(2,2,6,6-tetramethylpiperidin-4-carboxylate), 4,4′-ethylenebis(2,2,6,6-tetramethylpiperazin-3-one), N-2,2,6,6-tetramethylpiperidin-4-yl-n-dodecylsuccinimide, N-1,2,2,6,6-pentamethylpiperidin-4-yl-n-dodecylsuccinimide, N-1-acetyl-2,2,6,6-tetramethylpiperidin-4-yln-dodecylsuccinimide, 1-acetyl3-dodecyl-7,7,9,9-tetramethyl-1,3,8-triazaspiro[4.5]decane-2,4dione, di-(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, di-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)succinate, 1-octyloxy-2,2,6,6-tetramethyl-4-hydroxy-piperidine, poly-{[6-tert-octylamino-s-triazin-2,4-diyl][2-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)imino-hexamethylene-[4-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)imino], 2,4,6-tris[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)-n-butylamino]-s-triazine, bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl)]sebacate; a mixture of bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]glutarate and bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]adipate; 1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine; bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]adipate; bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]glutarate; bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]succinate; a mixture of bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]glutarate and bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]succinate; 1-(4-octadecanoyloxy-2,2,6,6-tetramethylpiperidin-1-yloxy)-2-octadecanoyloxy-2-methylpropane; 1-(2-hydroxy-2-methylpropoxy)-4-[9-(methoxy-carbonyl)nonanoyloxy]-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-[5-(methoxy-carbonyl)pentanoyloxy]-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-[3-(methoxy-carbonyl)propionyloxy]-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-[4-(methoxy-carbonyl)-butyryloxy]-2,2,6,6-tetramethylpiperidine; condensation product of 4-hydroxy-1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidine with hexamethylene diisocyanate and terminated with methoxy; condensation product of 4-hydroxy-1-(2-hydroxy-ethoxy)-2,2,6,6-tetramethylpiperidine with hexamethylene diisocyanate and terminated with methoxy; and the condensation product of 4-hydroxy-1-(2-hydroxy-1-phenethoxy)-2,2,6,6-tetramethylpiperidine with hexamethylene diisocyanate and terminated with methoxy.

A most preferred hindered amine compound is bis(2,2,6,6-tetramethylpiperidin-4-yl)sebacate, bis(1,2,2,6,6-pentamethylpiperidin-4-yl)sebacate, di(1,2,2,6,6-pentamethylpiperidin-4-yl)(3,5-di-tert-butyl-4-hydroxybenzyl)butylmalonate, the polycondensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, the polycondensation product of 2,4-dichloro-6-tert-octylamino-s-triazine and 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine), N,N′,N″,N′″-tetrakis[(4,6-bis(butyl-(1,2,2,6,6-pentamethylpiperidin-4-yl)amino)-s-triazine-2-yl]-1,10-diamino-4,7-diazadecane. di-(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, di-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)succinate, 1-octyloxy-2,2,6,6-tetramethyl-4-hydroxy-piperidine, poly-{[6-tert-octylamino-s-triazin-2,4-diyl][2-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)imino-hexamethylene-[4-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)imino], 2,4,6-tris[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)-n-butylamino]-s-triazine, or 1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine.

The instant composition can additionally contain another UV absorber selected from the group consisting of the benzotriazoles, the s-triazines, the oxanilides, the salicylates, the hydroxybenzophenones, the benzoates and the α-cyanoacrylates.

Particularly, the instant composition may additionally contain an effective stabilizing amount of at least one other 2-hydroxyphenyl-2H-benzotriazole; another tris-aryl-s-triazine; or hindered amine or mixtures thereof.

Preferably, the 2-hydroxyphenyl-2H-benzotriazole is selected from the group consisting of

2-(2-hydroxy-3,5-di-tert-amylphenyl)-2H-benzotriazole;

2-[2-hydroxy-3,5-di(α,α-dimethylbenzyl)phenyl]-2H-benzotriazole;

2-[2-hydroxy-3-(α,α-dimethylbenzyl)-5-tert-octylphenyl]-2H-benzotriazole;

2-{2-hydroxy-3-tert-butyl-5-[2-(omega-hydroxy-octa(ethyleneoxy)carbonyl)ethyl]-phenyl}-2H-benzotriazole;

5-chloro-2-(2-hydroxy-3,5-di-tert-butylphenyl)-2H-benzotriazole;

5-chloro-2-(2-hydroxy-3-tert-butyl-5-methylphenyl)-2H-benzotriazole;

2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole; and

2-{2-hydroxy-3-tert-butyl-5-[2-(octyloxy)carbonyl)ethyl]phenyl}-2H-benzotriazole.

Preferably, the other tris-aryl-s-triazine is selected from the group consisting of

2,4-bis(2,4-dimethylphenyl)-6-(2-hydroxy-4-octyloxyphenyl)-s-triazine;

2,4-diphenyl-6-(2-hydroxy-4-hexyloxyphenyl)-s-triazine;

2,4-bis(2,4-dimethylphenyl)-6-[2-hydroxy-4-(3-do-/tri-decyloxy-2-hydroxypropoxy)-phenyl]-s-triazine;

2,4-bis(2,4-dimethylphenyl)-6-[2-hydroxy-4-(3-nonyloxy*-2-hydroxypropyloxy)-5-α-cumylphenyl]-s-triazine. (* denotes a mixture of octyloxy, nonyloxy and decyloxy groups.), and

2,4-bis(biphenylyl)-6-[2-hydroxy-4-(3-nonyloxy*-2-hydroxypropyloxy)phenyl]-s-triazine. (* denotes a mixture of octyloxy, nonyloxy and decyloxy groups.)

The instant compounds are often used in conjunction with one or more coadditive stabilizers where the coadditive stabilizer is a hindered phenolic antioxidant selected from the group consisting of neopentanetetrayl tetrakis(3,5-di-tert-butyl-4-hydroxy-hydrocinnamate, octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, 1,3,5-trimethyl-2,4,6-tris(3,5,-di-tert-butyl-4-hydroxybenzyl)benzene, 1,2-bis(3,5-di-tert-butyl-4-hydroxyhydrocinnamoyl)hydrazine, calcium [bis(monoethyl 3,5-di-tert-butyl-4-hydroxybenzyl)-phosphonate], 1,3,5-tris(3,5-di-tert-butyl-4-hydroxybenzyl)isocyanurate and 1,3,5-tris(3-hydroxy-4-tert-butyl-2,6-dimethylbenzyl)isocyanurate; or is an organophosphorus stabilizer selected from the group consisting of tris(2,4-di-tert-butylphenyl)phosphite, bis(2,4-di-tert-butyl-6-methylphenyl)ethyl phosphite, 2,2′,2″-nitrilo[triethyl-tris-(3,3′,5,5′-tetra-tert-butyl-1,1′-biphenyl-2,2′-diyl)phosphite], tetrakis(2,4-di-butylphenyl) 4,4′-biphenylenediphosphonite, tris(nonylphenyl)phosphite, bis(2,4-di-tert-butylphenyl)pentaerythrityl diphosphite, 2,2′-ethylidenebis(2,4-di-tert-butylphenyl)fluorophosphite and 2-butyl-2-ethylpropan-1,3-diyl 2,4,6-tri-tert-butylphenyl phosphite; or is 5,7-di-tert-butyl-3-(3,4-dimethylphenyl)-2H-benzofuran-2-one; or is N,N-dialkylhydroxylamine made by the direct oxidation of N,N-di(hydrogenated tallow)amine; or is a hindered amine selected from the group consisting of bis(2,2,6,6-tetramethylpiperidin-4-yl)sebacate, the polycondensation product of 1-(2-hydroxyethyl)-2,2,6,6-tetramethyl-4-hydroxypiperidine and succinic acid, N,N′,N″,N′″-tetrakis[4,6-bis(butyl-1,2,2,6,6-pentamethylpiperidin-4-yl)amino-s-triazin-2-yl]-1,10-diamino-4,7-diazadecane, the polycondensation product of 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine) and 2,4-dichloro-6-tert-octylamino-s-triazine, the polycondensation product of 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine)and 2,4-dichloro-6-morpholino-s-triazine, the polycondensation product of 4,4′-hexamethylenebis(amino-1,2,2,6,6-pentamethylpiperidine) and 2,4-dichloro-6-morpholino-s-triazine, 2,2,6,6-tetramethylpiperidin-4-yl octadecanoate, 3-dodecyl-1-(1-acetyl-2,2,6,6-tetramethylpiperidin-4-yl)-pyrrolidin-2,5-dione, 1,3,5-tris{N-cyclohexyl-N-[2-(2,2,6,6-tetramethylpiperazin-3-on-4-yl)ethyl]amino}-s-triazine, poly[methyl 3-(2,2,6,6-tetramethylpiperidin-4-yloxy)-propyl]siloxane, the polycondensation product of 2,4-dichloro-6-(2,2,6,6-tetramethylpiperidin-4-yl)butylamino)-s-triazine, 2,2′ethylene-bis{[2,4-(2,2,6,6-tetramethylpiperidin-4-yl)butylamino-s-triazin-6-yl]aminotrimethyleneamino}, oligomer of N-{[2-(N-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-4-yl}-N,N′-bis(2,2,6,6-tetramethylpiperidin-4-yl)-1,6-hexanediamine terminated with 2,4-bis(dibutylamino)-s-triazin-6-yl, N,N′,N″-tris{2,4-bis[N-(1,2,2,6,6-pentamethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine, N,N′,N′″-tris{2,4-bis[N-(1,2,2,6,6-pentamethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine and N,N′,N″,N′″-tetrakis{2,4-bis[N-(1,2,2,6,6-pentamethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine; or is another N-hydrocarbyloxy substituted hindered amines selected from the group consisting of bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)adipate, bis(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)adipate, bis(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, 1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl octadecanoate, N,N′,N″-tris{2,4-bis[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine, N,N′,N′″-tris{2,4-bis[N-(1-cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine and N,N′,N″,N′″-tetrakis(2,4-bis[N-(1cyclohexyloxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-6-yl )-3,3′-ethylenediiminodipropylamine; or a hydroxy substituted N-hydrocarbyloxy substituted hindered amine selected from the group consisting of bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl)]sebacate; a mixture of bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]glutarate and bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]adipate; 1-(2-hydroxy-2-methylpropoxy)-4-octadecanoyloxy-2,2,6,6-tetramethylpiperidine; bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]adipate; bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]glutarate; bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]succinate; a mixture of bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]glutarate and bis[1-(2-hydroxy-2-methylpropoxy)-2,2,6,6-tetramethylpiperidin-4-yl]succinate; 1-(4-octadecanoyloxy-2,2,6,6-tetramethylpiperidin-1-yloxy)-2-octadecanoyloxy-2-methylpropane; 1-(2-hydroxy-2-methylpropoxy)-4-[9-(methoxy-carbonyl)-nonanoyloxy]-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-[5-(methoxy-carbonyl)pentanoyloxy]-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-[3-(methoxy-carbonyl)propionyloxy]-2,2,6,6-tetramethylpiperidine; 1-(2-hydroxy-2-methylpropoxy)-4-[4-(methoxy-carbonyl)butyryloxy]-2,2,6,6-tetramethylpiperidine; or is a UV absorber selected from the group consisting of 2-(2-hydroxy-3,5-di-α-cumylphenyl)-2H-benzotriazole, 2-(2-hydroxy-5-methylphenyl)-2H-benzotriazole, 5-chloro-2-(2-hydroxy-3,5-di-tert-butylphenyl)-2H-benzotriazole, 2-(2-hydroxy-3,5di-tert-amylphenyl)-2H-benzotriazole, 2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, 2,4di-tert-butylphenyl 3,5-di-tert-butyl4-hydroxybenzoate, 2-hydroxy-4-n-octyloxybenzophenone, 2,4-bis(2,4-dimethyphenyl)-6-(2-hydroxy-4-octyloxyphenyl)-s-triazine, oligomer of N-{2-[(1-propoxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-4-yl}-N,N′-bis(1-propoxy-2,2,6,6-tetramethylpiperidin-4-yl)-1,6-hexanediamine terminated with 2,4-bis(dibutylamino)-s-triazin-6-yl, the condensation product of 2-morpholino-4,6-dichloro-s-triazine with N,N′-bis(1,2,2,6,6-pentamethylpiperidin-4-yl)-1,6-hexanediamine; or mixtures thereof.

Preferably the coadditive stabilizer is neopentanetetrayl tetrakis(3,5-di-tert-butyl-4-hydroxyhydrocinnamate, tris(2,4-di-tert-butylphenyl)phosphite, N,N-dialkylhydroxylamine made by the direct oxidation of N,N-di(hydrogenated tallow)amine, N,N′,N″,N′″-tetrakis[4,6-bis(butyl-1,2,2,6,6-pentamethylpiperidin-4-yl)amino-s-triazin-2-yl]-1,10-diamino-4,7-diazadecane, the polycondensation product of 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine) and 2,4-dichloro-6-tert-octylamino-s-triazine, the polycondensation product of 4,4′-hexamethylenebis(amino-2,2,6,6-tetramethylpiperidine) and 2,4-dichloro-6-morpholino-s-triazine, the polycondensation product of 4,4′-hexamethylenebis(amino-1,2,2,6,6-pentamethylpiperidine) and 2,4-dichloro-6-morpholino-s-triazine, oligomer of N-{[2-(N-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-4-yl}-N,N′-bis(2,2,6,6-tetramethylpiperidin-4-yl)-1,6-hexanediamine terminated with 2,4-bis(dibutylamino)-s-triazin-6-yl, N,N′,N″-tris{2,4-bis[N-(1,2,2,6,6-pentamethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine, N,N′,N′″-tris{2,4-bis[N-(1,2,2,6,6-pentamethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine and N,N′,N″,N′″-tetrakis{2,4-bis[N-(1,2,2,6,6-pentamethylpiperidin-4-yl)butylamino]-s-triazin-6-yl}-3,3′-ethylenediiminodipropylamine, oligomer of N-{2-[(1-propoxy-2,2,6,6-tetramethylpiperidin-4-yl)butylamino]-s-triazin-4-yl}-N,N′-bis(1-propoxy-2,2,6,6-tetramethylpiperidin-4-yl)-1,6-hexanediamine terminated with 2,4-bis(dibutylamino)-s-triazin-6-yl, or the condensation product of 2-morpholino-4,6-dichloro-s-triazine with N,N′-bis(1,2,2,6,6-pentamethylpiperidin-4-yl)-1,6-hexanediamine.

The alkyd resin lacquers which can be stabilized against the action of light and moisture in accordance with the instant invention are the conventional stoving lacquers which are used in particular for coating automobiles (automobile finishing lacquers), for example lacquers based on alkyd/melamine resins and alkyd/acrylic/melamine resins (see H. Wagner and H. F. Sarx, “Lackkunstharze” (1977), pages 99-123). Other crosslinking agents include glycouril resins, blocked isocyanates or epoxy resins.

The lacquers stabilized in accordance with the invention are suitable both for metal finish coatings and solid shade finishes, especially in the case of retouching finishes, as well as various coil coating applications. The lacquers stabilized in accordance with the invention are preferably applied in the conventional manner by two methods, either by the single-coat method or by the two-coat method. In the latter method, the pigment-containing base coat is applied first and then a covering coat of clear lacquer over it.

It is also to be noted that the compounds of the present invention are applicable for use in non-acid catalyzed thermoset resins such as epoxy, epoxy-polyester, vinyl, alkyd, acrylic and polyester resins, optionally modified with silicon, isocyanates or isocyanurates. The epoxy and epoxy-polyester resins are crosslinked with conventional crosslinkers such as acids, acid anhydrides, amines and the like. Correspondingly, the epoxide may be utilized as the crosslinking agent for various acrylic or polyester resin systems that have been modified by the presence of reactive groups on the backbone structure.

When used in two-coat finishes, the compounds of the instant invention can be incorporated in the clear coat or both in the clear coat and in the pigmented base coat.

When water-soluble, water miscible or water dispersible coating are desired ammonium salts of acid groups present in the resin are formed. Powder coating composition can be prepared by reacting glycidyl methacrylate with selected alcohol components.

The instant benzotriazoles are made by conventional methods for preparing such compounds. The usual procedure involves the diazotization of a substituted o-nitroaniline followed by coupling the resultant diazonium salt with a substituted phenol and reduction of the azobenzene intermediate to the corresponding desired benzotriazole. The starting materials for these benzotriazoles are largely items of commerce or can be prepared by normal methods of organic synthesis.

While the instant benzotriazoles with their enhanced durability are particularly suited for automotive coating applications, it is contemplated that they will also be espeically useful in other applications where their enhanced durability is required such as in solar films and the like.

The instant invention also pertains to candle wax compositions which comprises

(a) white and unscented, white and scented, dyed and unscented, dyed and scented, dipped and unscented or dipped and scented candle wax, and

(b) an effective stabilizing amount of a benzotriazole of formula I or II as described above alone or in combination with a hindered amine.

An effective amount of benzotriazole alone or plus the hindered amine in the candle wax is 0.01 to 10% by weight, preferably 0.1 to 2% by weight; and most preferably 0.1 to 0.5% by weight based on the wax. When a combination of benzotriazole and hindered amine are used, the weight ratio of benzotriazole to hindered amine is 10:1 to 1:10; preferably 4:1 to 1:4; most preferably 2:1 to 1:2 based on the candle wax.

It should be noted that candles contain a host of various components. The base materials may be made up of the following:

paraffin wax,

natural oils,

polyamide plus fatty acid/ester,

fatty acids such as stearin,

opacifiers,

beeswax,

glycerides plus oxidized wax,

alcohols, and

ethylene oligomers.

Candles also contain a number of additives such as the following:

mold release agents,

fragrances,

insect repellants or insecticides,

hardeners,

crystal modifiers,

clarifiers,

guttering reducers,

colorants,

f.p. control agents,

stretchability improvers,

gelling agents,

extrusion aids, and

vortex reducers.

Each of the various components are meant to control or modify the properties of the candle to insure proper burning, reduce channelling, aid in uniform melting, and the like. The colorants and fragrances obviously are there to provide the proper color, scent or other aesthetic appeal.

Of increasing importance are the transparent gel candles which look like clear glass, but which burn like a classical candle. As is discussed in detail in U.S. Pat. No. 5,879,694, the relevant parts of which are incorporated herein by reference, these gel candles usually contain a copolymer selected from the group consisting of a triblock, radial block, diblock or multiblock copolymer classically made up of at least two thermodynamically incompatible segments containing both hard and soft segments. Typical of such block copolymers is KRATON® (Shell Chemical Co.) which consists of block segments of styrene monomer units and rubber monomer or comonomer units. The most common structure found in KRATON® D series is a linear ABA block with styrene-butadiene-styrene (SBS) or styrene-isoprene-styrene (SIS).

Candles may also contain other stabilizers such as phenolic antioxidants, phosphites, hydroxylamines and the like, particularly phenolic antioxidants such as are described above.

The following examples are for illustrative purposes only and are not to be construed to limit the scope of the instant invention in any manner whatsoever.

EXAMPLE 1 5-(3-Pyridyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole

A flask equipped with a mechanical stirrer and an inert atmosphere with a Firestone® valve containing a mixture of 5-bromo-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl-2H-benzotriazole (2.6 g, 0.005 mol), pyridine-3-boronic propanediolcyclic ester (0.86 g, 0.00525 mol) and 200 mL of n-propanol is evacuated and filled three times with nitrogen. To this mixture is added palladium (II) diacetate (0.045 g, 0.0002 mol), triphenylphosphine (0.157 g, 0.0006 mol), 3 mL of 2M sodium carbonate (0.64 g, 0.012 mol) and 5 mL of water. The flask is then evacuated and filled three times with nitrogen. The reaction mixture is stirred for 15 minutes at room temperature and then heated to 91° C. The reaction mixture is held at 91° C. for two hours and then cooled to room temperature. The solvent is removed under vacuum and the residue is partitioned between diethyl ether (200 mL) and water (100 mL). The organic phase is separated and is extracted sequentially with 5% aqueous sodium bicarbonte (100 mL) and saturated aqueous sodium chloride (100 mL). The organic phase is dried over anhydrous sodium sulfate and the volatiles are removed under vacuum. The residue is purified by dry-column flash chromatography (toluene eluent followed by ethyl acetate eluent; silica gel) to give 2.14 g (82.6% yield) of a light yellow solid, melting at 126-128° C.

Analysis: Calcd for C₃₄H₃₈N₄O: C, 78.73; H, 7.38; N, 10.80. Found: C, 78.39; H, 7.36; N, 10.50.

¹Hnmr (CDCl₃): δ0.86 (s, 9H); 1.45 (s, 6H); 1.79 (s, 2H); 1.92 (s, 6H); 6.75 (dd, 1H); 7.06 (dd, 1H); 7.12 (t, 1H); 7.27 (t, 2H); 7.29 (multiplet, 1H); 7.44 (d, 1H); 7.48 (d, 1H); 7.49 (d, 2H); 7.73 (d, 1H); 8.53 (multiplet, 1H); 8.68 (d, 1H); 8.88 (d, 1H); 11.63 (s, 1H).

EXAMPLE 2 5-(3-Thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole

The procedure of Example 1 is followed using 5-bromo-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole (5.21 g, 0.01 mol), thiophene-3-boronic acid (1.34 g, 0.0105 mol), 250 mL of n-propanol, palladium(II) diacetate (0.090 g, 0.0004 mol), triphenylphosphine (0.315 g, 0.0012 mol), 6 mL of 2M sodium carbonate (1.27 g, 0.012 mol) and 5 mL of water. The residue is purified by dry-column flash chromatography (toluene eluent), followed by recrystallization from heptane to give 4.12 g (78.6% yield) of the title compound as a light yellow solid melting at 147-149° C.

Analysis: Calcd for C₃₃H₃₇N₃OS: C, 75.68; H, 7.12; N, 8.02; S, 6.12. Found: C, 75.81; H, 6.98; N, 7.99; S, 6.04.

¹Hnmr (CDCl₃): δ0.84 (s, 9H); 1.52 (s, 6H); 1.82 (s, 6H); 1.86 (s, 2H); 7.16-7.32 (overlapping m, 5H); 7.45 (dd, 1H); 7.48 (dd, 1H); 7.56 (dd, 1H); 7.63 (d, 1H); 7.73 (dd, 1H); 7.87 (d, 1H); 8.02 (d, 1H); 8.34 (d, 1H); 11.38 (s, 1H).

EXAMPLES 3-26

Following the general procedure of Example 1 using the starting intermediate 5-bromo-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl-2H-benzotriazole and selected heterocyclic boronic acids or dimethyl esters thereof as listed in the table below in the presence palladium (II) diacetate catalyst, the corresponding 5-heteroaryl substituted benzotriazole is prepared.

2-(2-Hydroxy-3-α-cumyl- 5-tert-octylphenyl- 2H-benzotriazole Heteroaryl Substituted by at Example Boronic Acid (Ester) 5-Position Benzo Ring  3 3-pyridyl 3-pyridyl  4 3-pyridyl (dimethyl) 3-pyridyl  5 4-pyridyl 4-pyridyl  6 5-methoxy-3-pyridyl 5-methoxy-3-pyridyl  7 2-furyl 2-furyl  8 3-formyl-2-furyl 3-formyl-2-furyl  9 4-methyl-2-furyl 4-methyl-2-furyl 10 3-furyl 3-furyl 11 2-thienyl 2-thienyl 12 5-bromo-2-thienyl 5-bromo-2-thienyl 13 3-formyl-2-thienyl 3-formyl-2-thienyl 14 5-formyl-2-thienyl 5-formyl-2-thienyl 15 5-methyl-2-thienyl 5-methyl-2-thienyl 16 5-acetyl-2-thienyl 5-acetyl-2-thienyl 17 5-chloro-2-thienyl 5-chloro-2-thienyl 18 2-formyl-3-thienyl 2-formyl-3-thienyl 19 1-triisopropyl- 1-triisopropylsilyl- silyl-3-pyrrolyl 3-pyrrolyl 20 1-tert-butoxy- 1-tert-butoxycarbonyl- carbonyl-2-pyrrolyl 2-pyrrolyl 21 5-indolyl 5-indolyl 22 8-quinolyl 8-quinolyl 23 3-thianaphthenyl 3-thianaphthenyl 24 2-selenophenyl 2-selenophenyl 25 2,4-di-benzyloxy- 2,4-di-benzyloxy- 5-pyrimidyl 5-pyrimidyl 26 2,4-dimethoxy- 2,4-dimethoxy- 5-pyrimidyl 5-pyrimidyl

EXAMPLE 27 2,5-Bis[2-(2-hydroxy-3-α-cumyl-5-tert-octyl-phenyl)-2H-benzotriazol-5-yl]thiophene

When following the general procedure of Example 1 using the starting intermediate 5-bromo-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole and thiophene-2,5-diboronic acid, the title compound is prepared.

EXAMPLE 28 Polycarbonate

The durability of representative instant benzotriazoles in thermoplastic substrates is determined by incorporating various test compounds into solvent cast films of polycarbonate resins. The free standing films are mounted into cardboard holders, secured in metal frames and exposed in an Atlas C165 Xenon-arc Weather-Ometer under dry conditions according to ASTM G26. Loss of UV absorber is determined by monitoring the loss of diagnostic UV absorption.

Polycarbonate flake (LEXAN® 145, General Electric) is dissolved in methylene chloride at room temperature along with between 1 and 3% by weight of test benzotriazole, based on the polycarbonate. Films are cast using a calibrated drawdown bar to prepare 1 mil thick film after drying.

The instant compounds are particularly efficacious when used in thermoplastic compositions, such as polycarbonate. This is shown by the reduction in absorbance loss after exposure to actinic radiation.

EXAMPLE 29 Polycarbonate

Polycarbonate films of about 1 mil thickness and containing a UV absorber are prepared by dissolving polycarbonate granules (LEXAN® 145, General Electric) and UV absorbers in methylene chloride and casting the films on a glass plate using a drawdown bar. The films are exposed for 750 hours in a Xenon Arc Weather-Ometer according to ASTM G26 test method and the color change (ΔYI) versus that for unexposed films are recorded below. The color measurements (yellowness index—YI) are carried out on an ACS spectrophotometer, small area view, spectral component included d/8, D65, 10° observer, YI 1925 for unexposed and exposed samples after 750 hours.

The instant compounds are particularly efficacious when used in thermoplastic compositions, such as polycarbonate. This is shown by the reduction of yellowing (ΔYI) after exposure to actinic radiation.

EXAMPLE 30 Poly(methyl methacrylate)

The durability of representative instant benzotriazoles in thermoplastic substrates is determined by incorporating various test compounds into solvent cast films of a poly(methyl methacrylate) (PMMA) resin. The free standing films are mounted into cardboard holders, secured in metal frames and exposed in an Atlas C165 Xenon-arc Weather-Ometer under dry conditions according to ASTM G26. Loss of UV absorber is determined by monitoring the loss of diagnostic UV absorption as described earlier. Performance is measured by a change in color or the physical integrity of the film, or in loss of absorbance of the UV absorber at λmax.

Poly(methyl methacrylate), medium molecular weight, Aldrich, is dissolved in methylene chloride at room temperature along with between 1 and 3% by weight of test benzotriazole, based on the PMMA resin. Films are cast using a calibrated drawdown bar to prepare 1 mil thick film after drying.

The instant compounds are particularly efficacious when used in thermoplastic compositions, such as poly(methyl methacrylate). This is shown by the reduction in absorbance loss after exposure to actinic radiation.

EXAMPLE 31 Incorporation into Photographic Layers

A gelatin coat of the following composition (per m²) is applied in the customary manner to a polyester base.

Components Amount Gelatin 1200 mg  Tricresyl Phosphate 510 mg Hardener*  40 mg Wetting Agent** 100 mg Test UV Absorber 400 mg *potassium salt of 2-hydroxy-4,6-dichloro-s-triazine **sodium 4,8-diisobutylnaphthalene-2-sulfonate

The gelatin coats are dried at 20° C. for seven days.

When the instant UV absorbers are used, clear transparent coats are obtained which are suitable for photographic recording material for example as a UV filter coat. This is seen by measuring the % Change in Initial Optical Density (2.0) after UV exposure. The instant compounds when used in a photographic layer are extremely photostable.

EXAMPLE 32 Automotive Coating Compositions

To ascertain the effect on thermal durability and loss rate from a high solids thermoset acrylic coating containing an instant benzotriazole UV absorber, the following tests are carried out.

A high solids thermoset acrylic clear coat is prepared by mixing an experimental acrylic polyol resin and hexamethoxymethylmelamine (Resimene® 747, Monsanto) at a solids ratio of 60/40. The dodecylbenzene sulfonic acid catalyst (Nacure® 5225; King Industries) is added at 0.70% by weight. A flow aid Modaflow® (Monsanto) is added at 0.25% by weight to form a model acrylic melamine resin system.

The model clear coat is reduced with xylene to a viscosity of 26-27 second using a Zahn #2 cup and applied via a conventional air spray at 50 psi (3.5 Kg/cm²) over a 1″×3″ (2.54 cm×7.62 cm) quartz slide. Cure is achieved by baking the slide for 30 minutes at 260° F. (127° C.). The clear coat is stabilized with 1% by weight of a hindered amine light stabilizer, bis-(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, (TINUVIN® 123, Ciba). The various test benzotriazole UV absorbers are incorporated at the 5 mmol % by weight in the clear coat. The film thickness on the quartz slides range from 1.15 to 1.41 mils (0.029 to 0.036 mm).

The films on the quartz slides are weathered according to the following conditions in Xenon Arc Weather-Ometer with a controlled irradiance at 6500 W, using inner quartz and outer borosilicate S-type filter. The irradiation cycle is as follows: 40 minutes of straight irradiation with no water spray, followed by 20 minutes of light plus front spray, followed by 60 minutes of light irradiation and finally by 60 minutes dart plus rear spray (condensation). The setting is at 0.55 W/M² at 340 nm, 1.98 kJ/hour. In the light cycle the black panel temperature is controlled at 70±2° C. The relative humidity in the light cycle is in the range of 50-55% and in the dark cycle 100%. The absorbance of the long wavelength UV band as a function of Xenon arc weathering hours are recorded.

To follow the loss of UV absorbers from the clear coats, UV spectra are measured initially and after weathering at regular time intervals. The UV spectrophotometer measures absorbance linearly up to 5.5 absorbance units using a reference beam attenuation technique.

It is assumed that the degradation products from the UV absorber do not contribute to the UV spectrum. This is tested by following the ratio of absorbance of the band at about 300 nm and the band at about 340 nm. The ratio does not change upon weathering the sample. This suggests that the UV spectrum of the weathered films correspond to the amount of UV absorber remaining in the film with very little if any contribution to the spectrum by photo degradants.

Representative benzotriazole test compounds are incorporated into a high solid thermoset acrylic melamine resin at a concentration of 3% by weight to give equal molar concentrations of the test benzotriazole in equal film thickness and sufficient to give a starting absorbance of approximately 2.0 absorbance units.

The instant benzotriazoles are especially durable in automotive coatings as judged by low loss rates.

The instant compounds are also useful in the protection of candle wax from discoloration.

Raw Materials for Candle Wax

Fully refined wax with a melting point of 137-141° C. and <0.5% oil content is obtained from the Astor Wax Company.

Dyes are supplied by French Color and Chemical Corporation.

Additional wax samples are supplied by the Candle Corporation of America. These samples contained red, green or yellow dyes and fragrances.

Additional wax samples are also supplied by the Candle-Lite Corporation. These scented samples are white, pink or gray.

The UV absorbers and hindered amine stabilizers are obtained from the Ciba Speciality Chemicals Corporation.

Sample Preparation

The wax samples obtained from the Candle Corporation of America already contain a dye and a fragrance (scent). In these cases, the wax is melted and the appropriate stabilizer(s) is (are) added and dissolved in the molten wax. The stabilized wax is then poured into a mold (7″×8.5″×0.25″; 17.78 cm×21.59 cm×0.635 cm) giving a wax plaque.

To the wax samples obtained from the Astor Wax Company after melting are added 0.001% by weight of the test dyes to give a dyed candle wax base. To the dyed wax base after melting is (are) added the appropriate stabilizer(s). The melted stabilized and dyed wax is then poured into the mold described above to give a wax plaque.

Sample Exposure

The wax plaques described above are cut into eight equal pieces (3.5″×2.125″; 8.89 cm×5.40 cm). Triplicate samples of each are exposed under a bank of six (6) cool-white fluorescent lamps (40 watts) or under a bank of six (6) UV lamps having a wavelength of 368 nm with the test samples being twelve (12) inches (30.48 cm) below the lamps.

Dye color fade (or color change) is measured by a Macbeth ColorEye Spectrophotometer with a 6 inch integrating sphere. The conditions are: 10 degree observer, D65 illuminant and 8 degree viewing angle.

Initial color measurements are taken using the above parameters. The L, a and b values are calculated using the CIE system from the reflectance values. YI is calculated from the L, a and b values. Subsequent measurements are taken at specified intervals. Delta L, a, b and YI values are simply the difference between the initial values and the values at each interval. Delta(Δ) E is calculated as follows:

[(Delta L)²+(Delta a)²+(Delta b)²]½=Delta E.

EXAMPLE 33 Color Change of a White Unscented Candle Wax under Fluorescent Lamp Exposure

A variety of different stabilizers are evaluated in a white unscented candle wax under fluorescent lamp exposure. The stabilizers include a compound of Example 2 alone or with a hindered amine such as bis(1,2,2,6,6-pentamethylpiperidin-4-yl) sebacate, TINUVIN® 292, CIBA or bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, TINUVIN® 123, CIBA. The ΔE values represent the change in color after exposure. A low ΔE value indicates less change in color and is highly desired.

The instant compound alone or with the hindered amine provides excellent protection to the white unscented candle wax from discoloration.

EXAMPLE 34 Color Fade of Green Scented Candle Wax ynder UV Lamp Exposure

A variety of different stabilizers are evaluated in green scented candle wax obtained from the Candle Corporation of America under UV lamp exposure at 368 nm wavelength. The stabilizers include a compound of Example 1 alone or with a hindered amine such as bis(1,2,2,6,6-pentamethylpiperidin-4-yl)sebacate, TINUVIN® 292, CIBA or bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl)sebacate, TINUVIN® 123, CIBA. The ΔE values represent the change in color after exposure. A low ΔE value indicates less change in color and is highly desired.

The instant compound alone or with the hindered amine provides excellent protection to the green scented candle wax from dye fade.

EXAMPLE 35 Color Fade of a Blue Unscented Candle Wax under UV Lamp Exposure

A variety of different stabilizers are evaluated in blue unscented candle wax under UV lamp exposure at 368 nm wavelength. The stabilizers include a compound of Example 1 alone or with a hindered amine such as bis(1,2,2,6,6-pentamethylpiperidin-4-yl) sebacate, TINUVIN® 292, CIBA or bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN® 123, CIBA. The ΔE values represent the change in color after exposure. A low ΔE value indicates less change in color and is highly desired.

The instant compound alone or with the hindered amine provides excellent protection to the blue unscented candle wax from dye fade.

EXAMPLE 36 Color Fade of Pink Scented Candle Wax under Fluorescent Lamp Exposure

Different stabilizers are evaluated in pink scented candle wax obtained from the Candle-Lite Corporation under fluorescent lamp exposure. The ΔE values represent the change in color after the indicated days of exposure. A low ΔE value indicates less change in color and is highly desired.

ΔE After

Sample* (wt % add) 8.9 days 11.8 days 22.3 days Blank (no add) 8.1 10.22 12.12 A (0.3%) 8.72 10.48 12.91 A (0.15%) + 1.77 2.49 4.16 B (0.15%) *A is bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN ® 123, CIBA). B is 5-(3-thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, Compound of Example 2.

These data show that a hindered amine substituted on the N-atom with an alkoxy moiety (Compound A) in combination with an instant UV absorber protects the pink scented candle wax far better than the hindered amine alone.

EXAMPLE 37 Color Fade of Pink Scented Candle Wax under UV Lamp Exposure

A variety of different stabilizers are evaluated in pink scented candle wax obtained from the Candle-Lite Corporation under UV lamp exposure. The ΔE values represent the change in color after the indicated days of exposure. A low ΔE value indicates less change in color and is highly desired.

ΔE After

Sample* (wt % add) 7.6 days 13.5 days 36.7 days Blank (no add) 16.16 16.44 20.27 A (0.3%) 13.93 15.20 15.88 C (0.15%) + 8.93 7.72 9.62 D (0.15%) A (0.15%) + 3.27 4.99 7.82 B (0.15%) *A is bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN ® 123, CIBA). B is 5-(3-thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, Compound of Example 2. C is 2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole, TINUVIN ® 329, CIBA. D is 4-octyloxy-2-hydroxybenzophenone, CHIMASSORB ® 81, CIBA.

These data show that a hindered amine substituted on the N-atom with an alkoxy moiety (Compound A) in combination with an instant UV absorber protects the pink scented candle wax far better than conventional UV absorbers.

EXAMPLE 38 Color Fade of Gray Scented Candle Wax under Fluorescent Lamp Exposure

A variety of different stabilizers are evaluated in gray scented candle wax obtained from the Candle-Lite Corporation under fluorescent lamp exposure. The ΔE values represent the change in color after the indicated days of exposure. A low ΔE value indicates less change in color and is highly desired.

ΔE After

Sample* (wt % add) 4.9 days 10.9 days 33.9 days Blank (no add) 9.66 11.97 16.01 A (0.3%) 9.67 10.89 11.32 C (0.15%) + 1.56 4.33 8.52 D (0.15%) A (0.15%) + 0.91 1.66 3.56 B (0.15%) *A is bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN ® 123, CIBA). B is 5-(3-thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, Compound of Example 2. C is 2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole, TINUVIN ® 329, CIBA. D is 4-octyloxy-2-hydroxybenzophenone, CHIMASSORB ® 81, CIBA.

These data show that a hindered amine substituted on the N-atom with an alkoxy moiety (Compound A) in combination with an instant UV absorber protects the gray scented candle wax far better than conventional UV absorbers.

EXAMPLE 39 Color Fade of Gray Scented Candle Wax under UV Lamp Exposure

A variety of different stabilizers are evaluated in white scented candle wax obtained from the Candle-Lite Corporation under UV lamp exposure. The ΔE values represent the change in color after the indicated days of exposure. A low ΔE value indicates less change in color and is highly desired.

ΔE After

Sample* (wt % add) 2.8 days 8.9 days 22.6 days Blank (no add) 22.20 28.98 30.07 A (0.3%) 20.83 27.37 25.70 C (0.15%) + 2.30 7.06 10.96 D (0.15%) A (0.15%) + 1.70 3.47 5.11 E (0.15%) A (0.15%) + 1.05 2.51 3.91 B (0.15%) *A is bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN ® 123, CIBA). B is 5-(3-thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, Compound of Example 2. C is 2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole, TINUVIN ® 329, CIBA. D is 4-octyloxy-2-hydroxybenzophenone, CHIMASSORB ® 81, CIBA. E is octyl 3-(benzotriazol-2-yl)-5-tert-butyl-4-hydroxyhydrocinnamate, TINUVIN ® 384, CIBA.

These data show that a hindered amine substituted on the N-atom with an alkoxy moiety (Compound A) in combination with an instant UV absorber protects the gray scented candle wax far better than conventional UV absorbers.

EXAMPLE 40 Color Fade of White Scented Candle Wax under Fluorescent Lamp Exposure

A variety of different stabilizers are evaluated in white scented candle wax obtained from the Candle-Lite Corporation under fluorescent lamp exposure. The ΔE values represent the change in color after the indicated days of exposure. A low ΔE value indicates less change in color and is highly desired.

ΔE After

Sample* (wt % add) 4.0 days 14.7 days 33.0 days Blank (no add) 27.56 33.74 34.68 B (0.3%) 13.31 22.24 26.35 C (0.15%) + 18.66 25.28 25.09 F (0.15%) C (0.15%) + 9.39 17.68 21.24 D (0.15%) A (0.15%) + 5.16 7.62 10.27 E (0.15%) A (0.15%) + 2.09 4.58 6.82 B (0.15%) *A is bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN ® 123, CIBA). B is 5-(3-thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, Compound of Example 2. C is 2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole, TINUVIN ® 329, CIBA. D is 4-octyloxy-2-hydroxybenzophenone, CHIMASSORB ® 81, CIBA. E is octyl 3-(benzotriazol-2-yl)-5-tert-butyl-4-hydroxyhydrocinnamate, TINUVIN ® 384, CIBA. F is bis(1,2,2,6,6-pentamethylpiperidin-4-yl) sebacate, TINUVIN ® 292, CIBA.

These data show that a hindered amine substituted on the N-atom with an alkoxy moiety (Compound A) in combination with an instant UV absorber protects the white scented candle wax far better than conventional UV absorbers.

EXAMPLE 41 Color Fade of White Scented Candle Wax under UV Lamp Exposure

A variety of different stabilizers are evaluated in gray scented candle wax obtained from the Candle-Lite Corporation under UV lamp exposure. The ΔE values represent the change in color after the indicated days of exposure. A low ΔE value indicates less change in color and is highly desired.

ΔE After

Sample* (wt % add) 5.9 days 16.6 days 35.0 days Blank (no add) 42.90 45.57 45.14 A (0.3%) 34.65 36.72 35.87 C (0.15%) + 24.48 28.86 27.80 F (0.15%) C (0.15%) + 21.17 28.41 30.99 D (0.15%) A (0.15%) + 13.34 16.50 18.16 E (0.15%) A (0.15%) + 4.57 8.08 11.08 B (0.15%) *A is bis(1-octyloxy-2,2,6,6-tetramethylpiperidin-4-yl) sebacate, TINUVIN ® 123, CIBA). B is 5-(3-thienyl)-2-(2-hydroxy-3-α-cumyl-5-tert-octylphenyl)-2H-benzotriazole, Compound of Example 2. C is 2-(2-hydroxy-5-tert-octylphenyl)-2H-benzotriazole, TINUVIN ® 329, CIBA. D is 4-octyloxy-2-hydroxybenzophenone, CHIMASSORB ® 81, CIBA. E is octyl 3-(benzotriazol-2-yl)-5-tert-butyl-4-hydroxyhydrocinnamate, TINUVIN ® 384, CIBA. F is bis(1,2,2,6,6-pentamethylpiperidin-4-yl) sebacate, TINUVIN ® 292, CIBA.

These data show that a hindered amine substituted on the N-atom with an alkoxy moiety (Compound A) in combination with an instant UV absorber protects the white scented candle wax far better than conventional UV absorbers.

EXAMPLE 42 5-Bromo-2-(2-hydroxy-3-α-cumyl-5-tert-octyl)phenyl)-2H-benzotriazole

This compound is an important intermediate for the preparation of the instant compounds by the Suzuki reaction by reaction with various arylboronic acids or esters.

(A) 2-Hydroxy-2′nitro-3-α-cumyl-4′-bromo-5-tert-octylazobenzene

Diazotization and coupling: 96% Sulfuric acid (243 g) is charged to a 2 L jacketed reactor and the internal temperature is adjusted to 20° C. 40% (wt/wt) nitrosylsulfuric acid (335.4 g in sulfuric acid, 1.06 mol) is added via an addition funnel keeping the internal temperature below 20° C. At the end of this dilution step, the solution is cooled to 0° C. and 217 g of 92.1% pure 4-bromo-2-nitroaniline (0.921 mol) is added in portions keeping the internal temperature between 15-20° C. The reaction mixture is stirred at room temperature for five hours. Water (674 g) is added over a two-hour period while keeping the internal temperature at 0-5° C. The solution is filtered through a coarse funnel and stored at 0° C. Titration of the diazo solution shows an sulfuric acid assay of 31.8% and a diazo assay of 17.9% (a yield of 86.2% of diazo compound based on the 4-bromo-2-nitroaniline).

In a 1 L jacketed reactor is added 94.9 g of 96% pure 2-α-cumyl-4-tert-octylphenol (0.281 mol) and 249.5 g of xylene followed by 4.1 g of HOSTAPUR® SAS 93. The mixture is dissolved at 28° C. and the temperature held there. The diazonium salt solution prepared above (723 g, 0.397 mol) is added to this solution over a period of six hours. At the end of the addition period, the transfer line is rinsed with 10.8 g of water and the reaction mixture is stirred for another 30 minutes. The reaction temperature is raised to 60° C. and stirring stopped. The mixture separated into two phases which are separated. 370.3 g of a xylene solution of 2-hydroxy-2′-nitro-3-α-cumyl-4′-phenyl-5-tert-octylazobenzene is obtained. The xylene is removed under vacuum and methanol is added to crystallize the product.

¹Hnmr (CDCl₃; 499.8494 MHz) δ0.83 (s, 9H); 1.44 (s, 6H); 1.78 (s, 2H); 1.79 (s, 6H); 7.13-7.28 (overlapping multiplets, 5H); 7.62 (d, 1H); 7.68 (d, 1H); 7.79 (dd, 1H); 7.85 (d, 1H); 8.19 (d, 1H); 12.94 (s, 1H).

(B) 5-Bromo-2-(2-hydroxy-3-α-cumyl-5-tert-octyl)phenyl)-2H-benzotriazole

To 2-butanol (200 mL) and sodium hydroxide (4.8 g, 0.1203 mol) at 94° C. in a 2 L jacketed reactor is added dropwise a solution of 2-hydroxy-2′nitro-3-α-cumyl-4′-phenyl-5-tert-octylazobenzene (24.4 g, 0.043 mol) and 2,3-dichloro-1,4-naphthoquinone (1.14 g, 0.005 mol) in methyl ethyl ketone (60 mL) over a period of 1.5 hours while maintaining the temperature of the reaction mixture over 90° C. Water and methyl ethyl ketone distill off during this period. After the reaction mixture is held for one hour at about 90° C., the reduction is complete as seen by a sample tested by HPLC. The reaction mixture is cooled to 30° C. and 31 mL of 30% sulfuric acid is added all at once. After further cooling to 5° C., the product precipitates along with a mixture of salts. The precipitate is isolated by filtration and freed of salts by repeated washing with water. Organic impurities are removed by washing with 200 mL of cold methanol. The title compound is obtained after drying in a yield of 73% (16.4 g) as a light beige solid melting at 113-117° C.

Analysis: Calcd for C₂₉H₃₄BrN₃O: C, 66.92; H, 6.58; N, 8.07; Br, 15.35. Found: C, 67.01; H, 6.35; N, 8.09; Br, 15.04.

¹Hnmr (CDCl₃; 499.8494 MHz) δ0.83 (s, 9H); 1.51 (s, 6H); 1.81 (s, 6H); 1.85 (s, 2H); 7.15-7.30 (overlapping multiplets, 5H); 7.51 (dd, 1H); 7.64 (d, 1H); 7.75 (d, 1H); 8.04 (d, 1H); 8.31 (d, 1H); 11.15 (s, 1H). 

What is claimed is:
 1. A compound of formula I or II

wherein R is 2-pyridyl, 3-pyridyl, 4-pyridyl, 2-thienyl, 3-thienyl, 2-furyl, 3-furyl, 2-pyrrolyl, 3-pyrrolyl, 3-thianaphthenyl, 8-quinolyl, 5-indolyl, 2-selenophenyl, or said pyridyl, thienyl, furyl, pyrrolyl, thianaphthenyl, quinolyl, indolyl or selenophenyl moiety substituted by one to five moieties selected from the group consisting of straight or branched chain alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, R₃S—, R₃SO—, R₃SO₂, aryl of 6 to 10 carbon atoms, perfluoroalkyl of 1 to 12 carbon atoms, halogen, nitro, cyano, carboxyl, triisopropylsilyl, formyl, acetyl, alkoxycarbonyl of 2 to 19 carbon atoms, hydroxyl, alkoxy of 1 to 18 carbon atoms, aryloxy of 6 to 10 carbon atoms, sulfato or phosphato, or where any two substituents from a benzo ring with the heteroaryl moiety to which they are attached, T is thien-2,5-diyl, R₃ is alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms or aryl of 6 to 10 carbon atoms, E₁ is hydrogen, straight or branched chain alkyl of 1 to 24 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 4 alkyl of 1 to 4 carbon atoms, E₂ is straight or branched chain alkyl of 1 to 24 carbon atoms, straight or branched chain alkenyl of 2 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 3 alkyl of 1 to 4 carbon atoms; or E₂ is alkyl of 1 to 24 carbon atoms or alkenyl of 2 to 18 carbon atoms substituted by one or more —OH, —OCOE₃, —NH₂, —NHCOE₃ or —COOE₃, or mixtures thereof; or said alkyl or said alkenyl interrupted by one or more —O— which can be unsubstituted or substituted by one or more —OH groups; where E₃ is hydrogen or alkyl of 1 to 24 carbon atoms, and where said alkyl is interrupted by one or more —O— and which can be substituted by one or more —OH, or —OR₂₁ groups where R₂₁ is alkyl of 1 to 12 carbon atoms; and with the proviso that, when E₁ is hydrogen, methyl or ethyl and E₂ is methyl or ethyl, R is not 2-pyridyl.
 2. A compound of formula I according to claim 1 wherein the heterocyclic group R is unsubstituted or is substituted by one moiety selected from the group consisting of methyl, formyl, chloro, acetyl, triisopropylsilyl or tert-butoxycarbonyl; and where E₁ and E₂ are independently straight or branched alkyl of 4 to 24 carbon atoms or phenylalkyl of 7 to 15 carbon atoms.
 3. A compound of formula I according to claim 1 wherein R is 3-pyridyl or 3-thienyl; E₁ is α-cumyl; and E₂ is tert-octyl.
 4. A process for the preparation of a compound of formula I or II

where R, T, E₁ and E₂ are defined in claim 1, which comprises reacting an arylboronic acid or ester of formula III or IV R—B(OR₁)(OR₂)  (II) (R₂O)(R₁O)B—T—B(OR₁)(OR₂)  (IV) where R₁ and R₂ are independently hydrogen, alkyl of 1 to 12 carbon atoms, or R₁ and R₂ together are alkylene of 2 to 4 carbon atoms; with a 5-substituted benzotriazole of formula V

where X is halogen or tosylate, and E₁ and E₂ are as defined in claim 1, in the presence of an effective amount of a palladium (II) catalyst at between 10 to 100° C.
 5. A process according to claim 4 where in the compound of formula V, X is bromo or iodo.
 6. A process according to claim 4 where the process is additionally carried out in the presence of a ligand.
 7. A process according to claim 6 wherein the ligand is triphenylphosphine, 2-(di-tert-butylphosphino)biphenyl, 1,1′-bis[2,4,8,10-tetrakis(tert-butyl)-dibenzo-[d,f][1,3,2]dioxaphosphepin-6-yl]ferrocene, tris(2,4-di-tert-butylphenyl)phosphite or 2,2′,2″-nitrilo[triethyl-tris(3,3′,5,5′-tetra-tert-butyl-1,1′biphenyl-2,2′-diyl)phosphite].
 8. A process according to claim 7 wherein the ligand is triphenylphosphine.
 9. A process according to claim 4 wherein the reaction takes place between 50 to 95° C.
 10. A composition stabilized against thermal, oxidative or light-induced degradation which comprises, (a) an organic material subject to thermal, oxidative or light-induced degradation, and (b) an effective stabilizing amount of a compound of formula I or II

wherein R is 2-pyridyl, 3-pyridyl, 4-pyridyl, 2-thienyl, 3-thienyl, 2-furyl, 3-furyl, 2-pyrrolyl, 3-pyrrolyl, 3-thianaphthenyl, 8-quinolyl, 5-indolyl, 2-selenophenyl, or said pyridyl, thienyl, furyl, pyrrolyl, thianaphthenyl, quinolyl, indolyl or selenophenyl moiety substituted by one to five moieties selected from the group consisting of straight or branched chain alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, R₃S—, R₃SO—, R₃SO₂, aryl of 6 to 10 carbon atoms, perfluoroalkyl of 1 to 12 carbon atoms, halogen, nitro, cyano, carboxyl, triisopropylsilyl, formyl, acetyl, alkoxycarbonyl of 2 to 19 carbon atoms, hydroxyl, alkoxy of 1 to 18 carbon atoms, aryloxy of 6 to 10 carbon atoms, sulfato or phosphato, or where any two substituents from a benzo ring with the heteroaryl moiety to which they are attached, T is thien-2,5-diyl, R₃ is alkyl of 1 to 18 carbon atoms, phenylalkyl of 7 to 15 carbon atoms or aryl of 6 to 10 carbon atoms, E₁ is hydrogen, straight or branched chain alkyl of 1 to 24 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 4 alkyl of 1 to 4 carbon atoms, E₂ is straight or branched chain alkyl of 1 to 24 carbon atoms, straight or branched chain alkenyl of 2 to 18 carbon atoms, cycloalkyl of 5 to 12 carbon atoms, phenylalkyl of 7 to 15 carbon atoms, phenyl, or said phenyl or said phenylalkyl substituted on the phenyl ring by 1 to 3 alkyl of 1 to 4 carbon atoms; or E₂ is alkyl of 1 to 24 carbon atoms or alkenyl of 2 to 18 carbon atoms substituted by one or more —OH, —OCOE₃, —NH₂, —NHCOE₃ or —COOE₃, or mixtures thereof; or said alkyl or said alkenyl interrupted by one or more —O— which can be unsubstituted or substituted by one or more —OH groups; where E₃ is hydrogen or alkyl of 1 to 24 carbon atoms, and where said alkyl is interrupted by one or more —O— and which can be substituted by one or more —OH or —OR₂₁ groups where R₂₁ is alkyl of 1 to 12 carbon atoms.
 11. A composition according to claim 10 wherein component (a) is a thermoplastic polyolefin, polyester, polyester urethane, polyether urethane or a water-borne coating.
 12. A composition according to claim 11 wherein component (a) is selected from the group consisting of polypropylene, thermoplastic polyolefin, low density polyethylene, medium density polyethylene, high density polyethylene, linear low density polyethylene, poly(butene-1), ethylene/vinyl acetate copolymer, ethylene/propylene copolymer, copolymers of ethylene or propylene with other alpha-olefins, copolymers of acrylonitrile-butadiene-styrene (ABS), copolymers of acrylonitrile and styrene that are impact modified with ethylene-propylene rubber or ethylene/propylene/alpha-olefin rubber or butyl acrylate rubber, blends of ABS and polycarbonate, blends of ABS and poly(vinyl chloride) (PVC), poly(vinyl chloride), copolymers of styrene and butadiene (HIPS), copolymers of styrene and butadiene that also contain ethylene-propylene rubber or ethylene/propylene/alpha-olefin rubber or butyl acrylate rubber, thermoplastic elastomers and thermoplastic vulcanizates.
 13. A composition according to claim 11 wherein component (a) is a polyester or polyether urethane or water-borne coating.
 14. A composition according to claim 10 which additionally contains an effective stabilizing amount of at least one coadditive stabilizer selected from the group consisting of the phenolic antioxidants, metal stearates, metal oxides, organophosphorus compounds, furanone antioxidants, hydroxylamines, UV absorbers, non-NOR hindered amines, NOR hindered amines and mixtures thereof.
 15. A composition according to claim 10 which is a stabilized stoving lacquer wherein component (a) is an acid catalyzed resin based on hot crosslinkable, acrylic, acrylic melamine, polyester, polyurethane, polyamide or alkyd resin.
 16. A composition according to claim 15 which additionally contains a UV absorber selected from the group consisting of the benzotriazoles, the s-triazines, the oxanilides, the salicylates, the hydroxybenzophenones, the benzoates and the α-cyanoacrylates.
 17. A composition according to claim 15 which is an enamel of high solids content for industrial finishes.
 18. A composition according to claim 17 which is a finishing enamel for automobiles.
 19. A composition according to claim 10 wherein component (a) is a polyolefin, polycarbonate, a styrenic, ABS, a nylon (polyamide), a polyester, a polyurethane, a polyacrylate, a rubber modified styrenic, poly(vinyl chloride), poly(vinyl butyral), polyacetal (polyoxymethylene), or other blends or copolymers such as poly(ethylene/1,4-cyclohexylenedimethylene terephthalate) PETG or an ethylene/acrylic acid copolymer or salts thereof (an ionomer).
 20. A composition according to claim 19 wherein the polymer is a polyester or a polyacrylate.
 21. A composition according to claim 20 wherein the polyester is poly(ethylene terephthalate), poly(butylene terephthalate) or poly(ethylene naphthalenedicarboxylate), or copolymer poly(ethylene/1,4-cyclohexylenedimethylene terephthalate) PETG.
 22. A composition according to claim 19 wherein component (a) is a polyolefin or polycarbonate.
 23. A composition according to claim 10 wherein component (a) is a photographic composition.
 24. A composition according to claim 10 wherein the organic material is a candle wax. 